Mechanical properties of electron beam welded dissimilar joints of TC17 and Ti60 alloys

被引：2
|
作者：
Chao Cheng [1 ,2 ]
Bingbing Yu [1 ]
Zhiyong Chen [1 ,2 ]
Jianrong Liu [1 ,2 ]
QingjiangWang [1 ,2 ]
机构：
[1] Institute of Metal Research, Chinese Academy of Sciences
[2] School of Materials Science and Engineering, University of Science and Technology of China
来源：
JournalofMaterialsScience&Technology | 2018年 / 34卷 / 10期
关键词：
Titanium alloy; Electron beam welding; Dissimilar joints; Mechanical properties;
D O I：
暂无
中图分类号：
TG456.3 [真空电子束焊];
学科分类号：
080201 ; 080503 ;
摘要：
Microstructure, hardness, tensile and high cycle fatigue（HCF） properties of the welded dissimilar joints of Ti60 and TC17 titanium alloys had been investigated in this study. A significant microstructural change was observed to occur after welding, with rod-like α and β phases in the fusion zone（FZ）, equiaxed αphases, fine α laths and β phases in the heat-affected zone（HAZ） of TC17 side and acicular martensiteα’ phases+ "ghost" α phases in the HAZ of Ti60 side. The microhardness across the joints exhibited an inhomogeneous distribution with the highest hardness of;04 HV in FZ and the lowest hardness of;04 HV in base material（BM） of Ti60. All the joints tested in tension fractured at BM of Ti60 side.Fatigue limits of the joints at 107 cycles were 425 MPa at room temperature and 380 MPa at 400℃,respectively. Welding micropores were found to be the main source of fatigue crack initiation.
引用
收藏
页码：1859 / 1866
页数：8
相关论文
共 50 条
  • [41] Cyclic deformation of dissimilar welded joints between Ti-6Al-4V and Ti17 alloys: Effect of strain ratio
    Wang, S. Q.
    Liu, J. H.
    Lu, Z. X.
    Chen, D. L.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2014, 598 : 122 - 134
  • [42] Study on the mechanical heterogeneity of electron beam welded thick TC4-DT joints
    Lu, Wei
    Li, Xiaoyan
    Lei, Yongping
    Shi, Yaowu
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2012, 540 : 135 - 141
  • [43] Microstructure, mechanical properties and post-weld heat treatments of dissimilar laser-welded Ti2AlNb/Ti60 sheet
    Yong Wu
    Gang Liu
    Zhi-Qiang Liu
    Ze-Jun Tang
    Bin Wang
    Rare Metals, 2023, 42 : 1332 - 1342
  • [44] Internal tensile properties of characteristic zones in the electron beam weldment of TC17 titanium alloy
    Xu, C.
    Liu, H. Q.
    Li, C. H.
    Yang, H. J.
    Shao, X. H.
    Ma, X. L.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2023, 875
  • [45] Microstructure and mechanical properties of rhenium and GH3128 superalloy dissimilar welded joints by electron beam welding
    Fan, Linhao
    Li, Dong
    Jia, Shudang
    Tao, Fu
    Chen, Jieshi
    MATERIALS RESEARCH EXPRESS, 2021, 8 (05)
  • [46] Influence of Plate Thickness on Microstructure and Mechanical Properties of Electron Beam Welding Joint of Ti60 Titanium Alloy
    Yu Bingbing
    Chen Zhiyong
    Li Jinwei
    Zhu Shaoxiang
    Liu Jianrong
    Li Yulan
    Wang Qingjiang
    Yang Rui
    RARE METAL MATERIALS AND ENGINEERING, 2017, 46 : 166 - 170
  • [47] Microstructural Evolution and Mechanical Properties of Electron Beam-Welded Ti70/TA5 Dissimilar Joint
    Wang, Donghui
    Wang, Shaogang
    Zhang, Wen
    JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 2021, 143 (02):
  • [48] Fatigue Behavior of Electron Beam Welded Dissimilar Metal Joints
    Calik, A.
    Karakas, M. S.
    Varol, R.
    WELDING JOURNAL, 2012, 91 (02) : 50S - 52S
  • [49] Improvement of mechanical property on TC17 welded joints with backing plates by TIG plus brazing hybrid welding
    Zhao, Xilong
    Lu, Xinhong
    Wang, Kun
    He, Feng
    WELDING IN THE WORLD, 2023, 67 (09) : 2123 - 2132
  • [50] Characteristics of Electron Beam Welded Ti & Ti alloys
    Mitchell, Ryan
    Short, Andrew
    Pasang, Timotius
    Littlefair, Guy
    STRUCTURAL INTEGRITY AND FAILURE, 2011, 275 : 81 - +
12345