Weibull analysis of fluidity and hardness of ultrasonical y degassed secondary Al7Si0.3Mg aluminum alloy

被引：1
作者：
?a?lar Yüksel [1 ]
机构：
[1] Atatürk University, Department of Metallurgical and Materials Engineering
来源：
China Foundry | 2019年 / 16卷 / 05期
关键词：
Weibull analysis; Weibull modulus; ultrasonic degassing; fluidity; hardness; aluminum;
D O I：
暂无
中图分类号：
TG146.21 []; TG24 [铸造工艺];
学科分类号：
080201 ; 080502 ; 080503 ;
摘要：
The influence of ultrasonic degassing process on fluidity and hardness of secondary Al7 Si0.3 Mg alloy castings was studied by Weibull analysis. This work makes a contribution about fluidity and hardness distribution of secondary aluminum alloys with ultrasonic degassing phenomena using a two-parameter form of Weibull analysis. Results show that both hardness and fluidity of alloy are improved after the ultrasonic degassing process. Average efficiency of ultrasonic degassing on fluidity measurements is 31.71%, whereas on hardness values is 8.48%. The Brinell hardness of 45.7 and fluidity of 19.5 of Weibull modulus were achieved as the most reliable and reproducible after 45 s ultrasonic degassing process against 15 s and 30 s ultrasonic degassing processes. The value of 70.08 HB is obtained from ultrosonic degassing, which is equivalent to sand casting of primary Al7 Si0.3 Mg aluminum alloy, and the highest value of 56.4 cm for 45 s after ultrasonic degassing of fluidity was measured.
引用
收藏
页码：352 / 357
页数：6
相关论文
共 21 条
  • [1] Effects of Ultrasonic Stirring on Microstructures of Al-7wt%Si Alloy Ingot[J] . Shucheng Dong,Wenquan Wang,Zimu Shi,Jianguo Li.Journal of Physics: Conference Series . 2018 (1)
  • [2] Quantification of Entrainment Damage in A356 Aluminum Alloy Castings[J] . Murat Tiryakio?lu,Pedram Yousefian,Paul D Eason.Metallurgical and Materials Transactions . 2018
  • [3] Effect of high power ultrasound on mechanical properties of Al-Si alloys[J] . N Srivastava,R Gupta,G P Chaudhari.IOP Conference Series: Materials Science and Engi . 2018 (1)
  • [4] Weibull analysis of effect of T6 heat treatment on fracture strength of AM60B magnesium alloy
    Shevidi, A. H.
    Taghiabadi, R.
    Razaghian, A.
    [J]. TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2018, 28 (01) : 20 - 29
  • [5] Ultrasonic melt processing in the low pressure investment casting of Al alloys[J] . J. Barbosa,H. Puga.Journal of Materials Processing Tech. . 2017
  • [6] The Effect of Iron Content on Microstructure and Mechanical Properties of A356 Cast Alloy
    Tuncay, Tansel
    Bayoglu, Samet
    [J]. METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2017, 48 (02): : 794 - 804
  • [7] Effect of high-intensity ultrasonic treatment on microstructure, hardness and wear behaviour of the hypereutectic Mg-5Si alloy[J] . M E Moussa,M A Waly,A M El-Sheikh.IOP Conference Series: Materials Science and Engi . 2016 (1)
  • [8] The effect of melt quality and quenching temperature on the Weibull distribution of tensile properties in aluminium alloys
    Tan, E.
    Tarakcilar, A. R.
    Dispinar, D.
    [J]. MATERIALWISSENSCHAFT UND WERKSTOFFTECHNIK, 2015, 46 (10) : 1005 - 1013
  • [9] Effect of ultrasonic degassing on performance of Al-based components
    Puga, H.
    Barbosa, J.
    Tuan, N. Q.
    Silva, F.
    [J]. TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2014, 24 (11) : 3459 - 3464
  • [10] The effect of melt quality and filtering on the Weibull distributions of tensile properties in Al–7%Si–Mg alloy castings[J] . G. Eisaabadi B.,P. Davami,S.K. Kim,M. Tiryakio?lu.Materials Science & Engineering A . 2013
123