Factors affecting the shrinkage of fly ash geopolymers

被引：0

作者：

Charoenchai Ridtirud ^{[1
]}

Prinya Chindaprasirt ^{[1
]}

Kedsarin Pimraksa ^{[2
]}

机构：

[1] Sustainable Infrastructure Research and Development Center,Department of Civil Engineering,Faculty of Engineering,Khon Kaen University

[2] Department of Industrial Chemistry,Faculty of Sciences,Chiang Mai University

来源：

InternationalJournalofMineralsMetallurgyandMaterials | 2011年 / 18卷 / 01期

关键词：

fly ash; inorganic polymers; shrinkage; compressive strength;

D O I：

暂无

中图分类号：

TB324 [高分子材料];

学科分类号：

070305 ;

摘要：

The shrinkage of fly ash geopolymers was studied in the present study.Fly ash was used as the source material for making the geopolymers.The effects of the concentration of NaOH,sodium silicate-to-NaOH ratio,liquid-to-ash ratio,curing temperature,and curing time on shrinkage were investigated.The geopolymers were cured at 25,40,and 60℃,respectively.The results indicate that the shrinkage of geopolymers is strongly dependent on curing temperature and liquid-to-ash ratio.The increase in shrinkage is associated with the low strength development of geopolymers.It is also found that NaOH concentration and sodium silicate-to-NaOH ratio also affect the shrinkage of geopolymers but to a lesser extent.

引用

页码：100 / 104

页数：5

共 9 条

[1]

Preparation of fly ash and rice husk ash geopolymer[J]. S. Detphan,P. Chindaprasirt.International Journal of Minerals Metallurgy and Materials. 2009(06)

[2] Workability and strength of lignite bottom ash geopolymer mortar [J].

Sathonsalowaphak, Apha ;

Chindaprasirt, Prinya ;

Pimraksa, Kedsarin .

JOURNAL OF HAZARDOUS MATERIALS, 2009, 168 (01) :44-50

[3] Geopolymeric binders with different fine fillers - Phase transformations at high temperatures [J].

Buchwald, Anja ;

Vicent, Monica ;

Kriegel, Ralf ;

Kaps, Christian ;

Monzo, Maria ;

Barba, Antonio .

APPLIED CLAY SCIENCE, 2009, 46 (02) :190-195

[4] Damage behavior of geopolymer composites exposed to elevated temperatures [J].

Kong, Daniel L. Y. ;

Sanjayan, Jay G. .

CEMENT & CONCRETE COMPOSITES, 2008, 30 (10) :986-991

[5] Comparative performance of geopolymers made with metakaolin and fly ash after exposure to elevated temperatures [J].

Kong, Daniel L. Y. ;

Sanjayan, Jay G. ;

Sagoe-Crentsil, Kwesi .

CEMENT AND CONCRETE RESEARCH, 2007, 37 (12) :1583-1589

[6]

Dissolution processes, hydrolysis and condensation reactions during geopolymer synthesis: Part II. High Si/Al ratio systems[J] . K. Sagoe-Crentsil,L. Weng.Journal of Materials Science . 2007 (9)

[7] Thermal behaviour of geopolymers prepared using class F fly ash and elevated temperature curing [J].

Bakharev, T .

CEMENT AND CONCRETE RESEARCH, 2006, 36 (06) :1134-1147

[8]

Mechanism of geopolymerization and factors influencing its development: a review[J] . Divya Khale,Rubina Chaudhary.Journal of Materials Science . 2007 (3)

[9]

Alkali-activated fly ash/slag cements[J] . Cement and Concrete Research . 2000 (10)

← 1 →