Structural & Magnetic Characterizations of NiLiZn Nanoferrites Synthesized by Co-precipitation Method

被引:0
作者
D.N. Rohadiana [1 ,2 ]
Z.A.Z. Jamal [1 ,2 ]
S.B. Jamaludin [1 ]
M.F. Bari [1 ]
J. Adnan [2 ]
机构
[1] Sustainable Engineering Research Cluster, Universiti Malaysia Perlis
[2] School of Microelectronic Engineering, Universiti Malaysia Perlis
关键词
Lithium nickel zinc ferrite; Co-precipitation; Crystal structure; Magnetic properties;
D O I
暂无
中图分类号
TB383.1 [];
学科分类号
070205 ; 080501 ; 1406 ;
摘要
Synthesis of Ni0.5LixZn(0.5-x)Fe2O4 nanoparticles with x=0, 0.1, 0.2, 0.3, 0.4 and 0.5 were realized via co-precipitation method. X-ray diffraction (XRD) and vibrating sample magnetometer (VSM) measurements were performed on the samples to determine the characteristics of the crystal structures and the magnetic properties of the samples, respectively. The spinel phase structures of the samples were confirmed by XRD analysis. Patterns of decreased lattice parameter and increased crystallite size values were observed by increasing the Li concentration at longer synthesis reaction periods. Similarly, for the magnetic properties, both the saturation magnetization (Ms) and coercivity (Hc) were found to vary with increasing patterns at higher Li doping levels and longer synthesis reaction periods. The results and mechanisms concerned were discussed.
引用
收藏
页码:991 / 995
页数:5
相关论文
共 2 条
  • [1] Physical and magnetic properties of calcium-substituted Li-Zn ferrite
    Sattar, A. A.
    El-Sayed, H. M.
    Agami, W. R.
    [J]. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2007, 16 (05) : 573 - 577
  • [2] Applications of magnetic nanoparticles in biomedicine .2 Pankhurst QA,Connolly J,Jones SK,et al. Journal of Physics D,Applied Physics . 2003