Influence of Water Vapor on the Isothermal Oxidation Behavior of Thermal Barrier Coatings

The oxidation of specimens with thermal barrier coating (TBC) consisted of nickel-base superalloy, low-pressure plasma sprayed Ni-28Cr-6AI-0.4Y (wt pct) bond coating and electron beam physical vapor deposited 7.5 wt pct yttria stabilized zirconia (YSZ) top coating was studied at 1050℃ respectively in flows of 02, and mixture of O2 and 5%H2O under atmospheric pressure. The thermal barrier coating has relatively low oxidation rate at 1050℃ in pure O2. Oxidation rate of thermal barrier coating in the atmosphere of O% and 5%H2O is increased The oxidation kinetics obeys almost linear law after long exposure time in the presence of 5% water vapor. Oxide formed along the interface between bond coat and top coat after oxidation at 1050℃ in pure O2 consisted of Al2O3, whereas interfacial scales formed after oxidation at 1050℃ in a mixture of O2 and 5%H2O were mainly composed of Ni(AI,Cr)2O4,NiO and AI2O3. It is suggested that the effect of water vapor on the oxidation of the NiCrAlY coating may be attributed