Effects of rapid quenching on structure and electrochemical characteristics of La0.5Ce0.2Mg0.3Co0.4Ni2.6-xMnx(x=0-0.4) electrode alloys

被引：4
作者：
张羊换 [1 ,2 ]
赵栋梁 [1 ]
董小平 [1 ,3 ]
祁焱 [1 ]
郭世海 [1 ]
王新林 [1 ]
机构：
[1] Department of Functional Material Research,Central Iron and Steel Research Institute
[2] School of Material,Inner Mongolia University of Science and Technology
[3] School of Materials Science and Engineering,University of Science and Technology Beijing
来源：
TransactionsofNonferrousMetalsSocietyofChina | 2009年 / 19卷 / 02期
基金：
中国国家自然科学基金;
关键词：
La-Mg-Ni system electrode alloy; rapid quenching; structure; electrochemical performance;
D O I：
暂无
中图分类号：
TG136.1 [];
学科分类号：
080502 ;
摘要：
The La-Mg-Ni system PuNi3-type La0.5Ce0.2Mg0.3Co0.4Ni2.6-xMnx(x=0,0.1,0.2,0.3,0.4) hydrogen storage alloys were prepared by casting and rapid quenching. The effects of the rapid quenching on the structure and electrochemical characteristics of the alloys were studied. The results obtained by XRD,SEM and TEM indicate that the as-cast and quenched alloys mainly consist of two major phases,(La,Mg)Ni3 and LaNi5,as well as a residual phase LaNi. The rapid quenching does not exert an obvious influence on the phase composition of the alloys,but it leads to an increase of the LaNi5 phase and a decrease of the(La,Mg)Ni3 phase. The as-quenched alloys have a nano-crystalline structure,and the grain sizes of the alloys are in the range of 20-30 nm. The results by the electrochemical measurements indicate that both the discharge capacity and the high rate discharge(HRD) ability of the alloy first increase and then decrease with the variety of quenching rate and obtain the maximum values at the special quenching rate which is changeable with the variety of Mn content. The rapid quenching significantly improves the cycle stabilities of the alloys,but it slightly impairs the activation capabilities of the alloys.
引用
收藏
页码：364 / 371
页数：8
相关论文
共 5 条
[1]  
XRD study on the electrochemical hydriding/dehydriding behavior of the La–Mg–Ni–Co-type hydrogen storage alloys[J] . Yongfeng Liu,Hongge Pan,Mingxia Gao,Yongquan Lei,Qidong Wang.Journal of Alloys and Compounds . 2005 (1)
[2]  
The electrochemical properties of La x Mg 3? x Ni 9 （ x =1.0–2.0） hydrogen storage alloys[J] . B. Liao,Y.Q. Lei,G.L. Lu,L.X. Chen,H.G. Pan,Q.D. Wang.Journal of Alloys and Compounds . 2003
[3]  
Hydrogen storage properties of new ternary system alloys: La 2 MgNi 9 , La 5 Mg 2 Ni 23 , La 3 MgNi 14[J] . T Kohno,H Yoshida,F Kawashima,T Inaba,I Sakai,M Yamamoto,M Kanda.Journal of Alloys and Compounds . 2000 (2)
[4]  
Structural investigation and hydrogen capacity of CaMg 2 Ni 9 : a new phase in the AB 2 C 9 system isostructural with LaMg 2 Ni 9[J] . K. Kadir,N. Kuriyama,T. Sakai,I. Uehara,L. Eriksson.Journal of Alloys and Compounds . 1999 (1)
[5]  
New approach for synthesizing Mg-based alloys[J] . Dalin Sun,Hirotoshi Enoki,Franz Gingl,Etsuo Akiba.Journal of Alloys and Compounds . 1999 (1)
1