DissolutionanddiffusionofTiO2intheCaO-Al2O3-SiO2slag

被引：1

作者：

Zhongshan Ren ^{[1
,2
]}

Xiaojun Hu ^{[1
]}

Xinmei Hou ^{[2
]}

Xiangxin Xue ^{[3
]}

Kuochih Chou ^{[1
,2
]}

机构：

[1] State Key Laboratory of Advanced Metallurgy,University of Science and Technology Beijing

[2] School of Metallurgical and Ecological Engineering,University of Science and Technology Beijing

[3] School of Materials and Metallurgy,Northeastern University

来源：

InternationalJournalofMineralsMetallurgyandMaterials | 2014年 / 21卷 / 04期

关键词：

slags; titanium dioxide; dissolution; diffusion; interface;

D O I：

暂无

中图分类号：

X756 [冶金工业];

学科分类号：

083002 ;

摘要：

The dissolution of TiO2 in the CaO-Al2O3-SiO2 slag under static conditions was studied in the temperature range from 1643 K to 1703 K. After TiO2 dissolved, the microstructure of the interface between TiO2 and the slag was observed by scanning electron microscopy, and the concentration profiles of Ti4+ and other ions across the TiO2/slag interfaces were analyzed by energy-dispersive X-ray spectroscopy. On the basis of these results, the dissolution behavior of TiO2 was evaluated, and the diffusivity of Ti4+ in the bulk slag was estimated. According to the Stokes–Einstein relation, the viscosity calculated by a previously reported model gave a diffusivity of Ti4+ ions greater than that estimated by the concentration profiles of Ti4+ ions. The mechanism of TiO2 dissolution in the CaO-Al2O3-SiO2 slag is discussed in detail.

引用

页码：345 / 352

页数：8

共 7 条

[1]

Dissolution of Al2TiO5 inclusions in CaO-SiO2-Al2O3 slags at 1823 K[J]. Fumitaka Tsukihashi,Hiroyuki Matsuura.International Journal of Minerals Metallurgy and Materials. 2011(06)

[2] IF钢中AlO-TiN复合夹杂生成机理研究 [J].

王敏 ;

包燕平 ;

崔衡 ;

吴华杰 ;

吴维双 .

钢铁研究学报, 2010, (07) :29-32+55

[3] Modeling the Viscosity of Alumino-Silicate Melt [J].

Zhang, Guo-Hua ;

Chou, Kuo-Chih .

STEEL RESEARCH INTERNATIONAL, 2013, 84 (07) :631-637

[4] Effects of additives and temperature on dissolution rate and diffusivity of lime in Al2O3-CaO-SiO2 based slags [J].

Amini, S. H. ;

Brungs, M. P. ;

Jahanshahi, S. ;

Ostrovski, O. .

METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2006, 37 (05) :773-780

[5] Multicomponent diffusion in molten slags [J].

Dolan, MD ;

Johnston, RF .

METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2004, 35 (04) :675-684

[6] Dissolution of alumina in mold fluxes [J].

Yu, X ;

Pomfret, RJ ;

Coley, KS .

METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 1997, 28 (02) :275-279

[7] MECHANISMS OF INCLUSION FORMATION IN AL-TI-SI-MN DEOXIDIZED STEEL WELD METALS [J].

KLUKEN, AO ;

GRONG, O .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1989, 20 (08) :1335-1349

← 1 →