Effect of Iron Oxides on Activity of Calcium Aluminate Clinker in CaO-Al2O3-SiO2 System

被引：0
作者：
Hai-yan YU [1 ]
Xiao-lin PAN [1 ]
Bao-wei LIU [2 ]
Bo WANG [1 ]
Shi-wen BI [1 ]
机构：
[1] School of Materials and Metallurgy,Northeastern University
[2] Guangxi Branch,CHALCO
来源：
JournalofIronandSteelResearch(International) | 2014年 / 21卷 / 11期
基金：
中国国家自然科学基金;
关键词：
FeO; Fe2O3; sintering; leaching; calcium aluminate; CaO-Al2O3-SiO2; system;
D O I：
暂无
中图分类号：
TQ174.4 [原料和辅助物料];
学科分类号：
0805 ; 080502 ;
摘要：
The sintering characteristics at 1 350℃and leaching property at 80℃ of calcium aluminate clinkers in the CaO-Al2O3-SiO2(C-A-S)system with different additions of FeO and Fe2O3 were investigated.FeO inhibits the conversion ofβ-Ca2SiO4toγ-Ca2SiO4 and makes the clinker not pulverizable.FeO and Fe2O3 inhibit the formation of CaAl2O4,but promote the formation of Ca12Al14O33.The interplanar spacing at(2 1 1)crystal face of Ca12Al14O33 in the clinker increases with the increase of FeO addition,which indicates that FeO forms solid solutions in Ca12Al14O33.The clinkers with Fe2O3 addition form a new phase Ca2Fe2O5,and the amount of Ca2Fe2O5 increases with the increase of Fe2O3 addition.Both FeO and Fe2O3 do not affect the Al2O3 leaching rate of calcium aluminate clinker in sodium carbonate solution,but they increase the molar ratio of caustic Na2 O to Al2O3 in the leached liquor.
引用
收藏
页码：990 / 994
页数：5
相关论文
共 12 条
  • [1] 氧化钠对CaO-Al2O3-SiO2三元系铝酸钙形成规律的影响（英文）
    于海燕
    潘晓林
    王波
    张武
    孙会兰
    毕诗文
    [J]. Transactions of Nonferrous Metals Society of China, 2012, 22 (12) : 3108 - 3112
  • [2] Na2O对含MgO铝酸钙炉渣相变规律和氧化铝浸出性能的影响（英文）
    王波
    孙会兰
    国栋
    张学政
    [J]. TransactionsofNonferrousMetalsSocietyofChina, 2011, 21 (12) : 2752 - 2757
  • [3] Chemical activation of calcium aluminate cement composites cured at elevated temperature
    Mostafa, Nasser Y.
    Zaki, Z. I.
    Abd Elkader, Omar H.
    [J]. CEMENT & CONCRETE COMPOSITES, 2012, 34 (10) : 1187 - 1193
  • [4] Defluoridation of water using calcium aluminate material[J] . Nikita Sakhare,S. Lunge,S. Rayalu,S. Bakardjiva,J. Subrt,Sukumar Devotta,Nitin Labhsetwar.Chemical Engineering Journal . 2012
  • [5] Synthesis, hydration and sintering of calcium aluminate nanopowder for advanced applications[J] . Mahmoud F. Zawrah,Adel B. Shehata,Esam A. Kishar,Randa N. Yamani.Comptes rendus - Chimie . 2010 (6)
  • [6] Investigation of a high stable β-cristobalite ceramic powder from CaO–Al 2 O 3 –SiO 2 system[J] . Journal of the European Ceramic Society . 2009 (14)
  • [7] Crystallization and sintering characteristics of CaO–Al 2 O 3 –SiO 2 glasses in the presence of TiO 2 , CaF 2 and ZrO 2[J] . S. Banijamali,B. Eftekhari Yekta,H.R. Rezaie,V.K. Marghussian.Thermochimica Acta . 2009 (1)
  • [8] Solid Solutions of Calcium Aluminates C 3 A, C 12 A 7 and CA with Sodium Oxide[J] . Journal of Thermal Analysis and Calorimetry . 2004 (3)
  • [9] Characteristics of long afterglow phosphorescent calcium aluminate crystals for fluorescence thermometer application[J] . H. Kubo,H. Aizawa,T. Katsumata,S. Komuro,T. Morikawa.Journal of Crystal Growth . 2004 (1)
  • [10] Kinetics and mechanism of formation of tricalcium aluminate, Ca 3 Al 2 O 6[J] . B.M. Mohamed,J.H. Sharp.Thermochimica Acta . 2002 (1)
12