Effect of rheo-diecast process on the mechanical properties of A390 alloy by serpentine channel

被引：0

作者：

Kunhyok Ri ^{[1
,2
]}

Wei-min Mao ^{[1
]}

Zhi-kai Zheng ^{[1
]}

Myongsik Kim ^{[2
]}

Yongho Sin ^{[2
]}

机构：

[1] School of Materials Science and Engineering, University of Science and Technology Beijing

[2] School of Material Engineering, Pyongyang Machinery University

来源：

InternationalJournalofMineralsMetallurgyandMaterials | 2016年 / 23卷 / 10期

基金：

中国国家自然科学基金;

关键词：

aluminum alloys; diecasting; rheo-casting; microstructure; mechanical properties;

D O I：

暂无

中图分类号：

TG249.2 [压力铸造];

学科分类号：

080201 ; 080503 ;

摘要：

In this paper, the effects of rheo-diecast process parameters and T6 heat treatment on the microstructure and mechanical properties of the rheo-diecasting(RDC) semi-solid A390 alloy prepared through pure copper serpentine channel were investigated. The results indicate that the mechanical properties of the RDC samples change with the pouring temperature and injection pressure. In this case, a lower pouring temperature results in better tensile strength and elongation of the RDC A390 alloy; however, the tensile strength and elongation decrease when the pouring temperature decreases to 660°C. Higher injection pressures result in the improved mechanical properties of the RDC A390 alloy. To some extent, T6 heat treatment improves the tensile strength and ductility of the RDC A390 alloy compared to those of the non-heat treated alloy. However, when the pouring temperature and injection pressure are greater than 670°C and 70 MPa, respectively, the mechanical properties are sharply diminished.

引用

页码：1177 / 1186

页数：10

共 12 条

[1] Refinement of primary Si grains of A390 alloy slurry through serpentine channel pouring process[J]. Zhi-kai Zheng,Wei-min Mao,Bing-quan Yan,Rui Yue,Zhi-yong Liu.China Foundry. 2015(06)
[2] 浇注温度对合金熔体冷却规律和半固态组织的影响
张帆
康永林
杨柳青
丁瑞华
[J]. 北京科技大学学报, 2010, 32 (11) : 1453 - 1458
[3] Semi-solid processing of hypereutectic A390 alloys using novel rheoforming process[J]. M.TEBIB,J.B.MORIN,F.A JERSCH,X.GRANT CHEN.Transactions of Nonferrous Metals Society of China. 2010(09)
[4] Microstructure and mechanical properties of rheo-diecasted A390 alloy
赵君文
吴树森
[J]. TransactionsofNonferrousMetalsSocietyofChina, 2010, 20(S3) (S3) : 754 - 757
[5] Hardness and Wear Behaviour of Semi-Solid Cast A390 Alloy Reinforced with Al2O3 and TiO2 Nanoparticles
El Mahallawi, I.
Shash, Y.
Rashad, R. M.
Abdelaziz, M. H.
Mayer, J.
Schwedt, A.
[J]. ARABIAN JOURNAL FOR SCIENCE AND ENGINEERING, 2014, 39 (06) : 5171 - 5184
[6] Effect of isothermal ageing on the semi-solid microstructure of rheoprocessed and partially remelted of A390 alloy with 10% Mg addition
Hekmat-Ardakan, Alireza
Ajersch, Frank
[J]. MATERIALS CHARACTERIZATION, 2010, 61 (08) : 778 - 785
[7] Cooling slope casting and thixoforming of hypereutectic A390 alloy[J] . Yücel Birol.Journal of Materials Processing Tech. . 2007 (1)
[8] An overview of the development of Al-Si-alloy based material for engine applications
Ye, HZ
[J]. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2003, 12 (03) : 288 - 297
[9] Effect of composition and processing route on the wear behaviour of Al–Si alloys[J] . L Lasa,J.M Rodriguez-Ibabe.Scripta Materialia . 2002 (6)
[10] Thixoforming of an automotive part in A390 hypereutectic Al–Si alloy[J] . P. Kapranos,D.H. Kirkwood,H.V. Atkinson,J.T. Rheinlander,J.J. Bentzen,P.T. Toft,C.P. Debel,G. Laslaz,L. Maenner,S. Blais,J.M. Rodriguez-Ibabe,L. Lasa,P. Giordano,G. Chiarmetta,A. Giese.Journal of Materials Processing Tech. . 2002 (2)

← 1 2 →