Wear mechanism and microstructures of Mo-implanted 4Cr5MoV1Si steel
被引：0
作者：
YANG JianHua ZHANG TongHe Department of Physics Nantong Institute of Technology Nantong Radiation Beam and Materials Engineering Lab Beijing Normal University Beijing
[1
,2
,2
,1
,2260072
,100875
]
机构：
关键词：
Ion implantation;
Wear resistance;
Steel;
Microstructure;
D O I：
暂无
中图分类号：
TG174.44 [金属复层保护];
学科分类号：
080503 ;
摘要：
Mo ions extracted from a metal vapor vacuum arc ion source (MEVVA) were implanted into 4Cr5MoV1Si(H13) steel samples with a high implantation dose of 5×1017cm-2 and a pulsed ion beam flux of about 300 μA·cm-2·An optical interference microscope and pin-on-disc apparatus were used to investigate the wear and friction characteristics of the steel. The results from Rutherford backscattering spectroscopy (RBS) and the collision theory demonstrated that the radiation enhanced diffusion gave great influence on the Mo profile. It was observed by X-ray photoelectron spectroscopy (XPS) and grazing-angle X-ray diffraction (GXRD) that carbide of Mo appeared in the doped region for the implantation at 48 kV. The results showed that improvement in the wear resistance of the Mo-implanted steel were mainly due to the formation of Mo2C in the doped zone and the implantation affected zone underneath. Oxidation resistance of the surface iron and the surface with small crystal grains gave influences on the wear resistance in a way.
引用
收藏
页码：155 / 159
页数：5
相关论文