Hot deformation behavior and process parameter optimization of Ti22Al25Nb using processing map

被引：1

作者：

Jing-Li Zhang ^{[1
]}

Hong-Zhen Guo ^{[1
]}

Hou-Quan Liang ^{[1
]}

机构：

[1] School of Materials Science and Engineering,Northwestern Polytechnical University

来源：

Rare Metals | 2016年 / 35卷 / 01期

基金：

中国国家自然科学基金;

关键词：

Ti22Al25Nb; Intermetallic; Processing map; Hot deformation behavior; Microstructure;

D O I：

暂无

中图分类号：

TG146.23 [];

学科分类号：

080502 ;

摘要：

The hot deformation behavior of Ti22A125 Nb was investigated by hot compression test.The flow stressstrain curves can be divided into two types:conventional dynamic recrystallization(DRX) and discontinuous DRX.The different softening mechanism and micro structure observation of conventional DRX and discontinuous DRX were analyzed.The processing map(PM) of Ti22A125 Nb was built to predict the safe deformation region.The optimal low strain rate domain(DOM I) with high power dissipation efficiency indicates the complete DRX.Additionally,in the high strain rate and low-temperature domain(DOM Ⅲ),the power dissipation efficiency is low and some adiabatic shear bands and glide bands are observed,which are unsafe and should be avoided.Finally,the DRX map was established.In DOM I,it reveals low dislocation density and high DRX content,which is in agreement with PM.

引用

页码：118 / 126

页数：9

共 15 条

[1] Ti3Al和Ti2AlNb基合金的研究与应用 [J].

张建伟 ;

李世琼 ;

梁晓波 ;

程云君 .

中国有色金属学报, 2010, 20(S1) (S1) :336-341

[2] 相场方法研究硬质颗粒钉扎的两相晶粒长大过程 [J].

高英俊 ;

张海林 ;

金星 ;

黄创高 ;

罗志荣 .

金属学报, 2009, 45 (10) :1190-1198

[3]

Effect of microstructure on tensile properties and fracture behavior of intermetallic Ti2AlNb alloys[J]. 李世琼 ,毛勇 ,张建伟 ,李俊涛 ,程云君 ,仲增墉.Transactions of Nonferrous Metals Society of China. 2002(04)

[4]

Discontinuous yielding in Ni-base superalloys during High-speed deformation[J] . Z.L. Zhao,Y.Q. Ning,HaZ. Guo,Z.K. Yao,M.W. Fu.Materials Science & Engineering A . 2014

[5]

Flow behavior and deformation mechanism in the isothermal compression of the TC8 titanium alloy[J] . K. Wang,M.Q. Li.Materials Science & Engineering A . 2014

[6]

A physically-based constitutive model for a typical nickel-based superalloy[J] . Y.C. Lin,Xiao-Min Chen,Dong-Xu Wen,Ming-Song Chen.Computational Materials Science . 2014

[7]

Hot deformation behavior and processing map of a typical Ni-based superalloy[J] . Dong-Xu Wen,Y.C. Lin,Hong-Bin Li,Xiao-Min Chen,Jiao Deng,Lei-Ting Li.Materials Science & Engineering A . 2014

[8]

Modeling Grain Boundary Motion and Dynamic Recrystallization in Pure Metals[J] . Julien Favre,Damien Fabrègue,David Piot,Ning Tang,Yuichiro Koizumi,Eric Maire,Akihiko Chiba.Metallurgical and Materials Transactions A . 2013 (13)

[9]

Hot deformation and processing map of a typical Al–Zn–Mg–Cu alloy[J] . Y.C. Lin,Lei-Ting Li,Yu-Chi Xia,Yu-Qiang Jiang.Journal of Alloys and Compounds . 2013

[10]

Flow behavior and hot workability of FGH4096 superalloys with different initial microstructures by using advanced processing maps[J] . Yongquan Ning,Zekun Yao,Zheng Yang,Hongzhen Guo,M.W. Fu.Materials Science & Engineering A . 2011

← 1 2 →