Effect of Pre-treatment on the Bi-2223/Ag Tapes Fabricated with Different Powders

被引：0
|
作者：
Li Mingya Chen Xingpin Ye Chengli Yu Liang Zhu Xu Northeastern University at Qinhuangdao Qinhuangdao China Chongqing University Chongqing China [1 ,2 ,1 ,1 ,1 ,1 ,66004 ,2 ,400044 ]
机构：
来源：
稀有金属材料与工程 | 2011年 / 40(S3)卷 / S3期
关键词：
pre-treatment; Bi-2223/Ag tapes; lead oxide compounds; critical current;
D O I：
暂无
中图分类号：
TB44 [粉末技术];
学科分类号：
0805 ;
摘要：
Samples of Bi-2223/Ag tapes fabricated with powders contained different lead oxide compounds were annealed at a temperature lower than the formation temperature of Bi-2223 phase before traditional heat treatment, which was called pretreatment. In pre-treatment stage, samples were heat treated at 780 ℃ in 8.5% O2, and the dwelling time is different. Experimental results show that pre-treatment had different influence on the formation and size of the Bi-2223 grains for tapes fabricated with powders contained different lead oxide compounds. For tapes contained both Ca2PbO4 and the 3321 phase, the decomposition of the 3321 phase enhanced the growth of Bi-2212 grains during pre-treatment process, which promoted the formation of Bi-2223 phase and enhanced the superconducting properties of Bi-2223/Ag tapes.
引用
收藏
页码：325 / 328
页数：4
相关论文
共 10 条
  • [1] Li M Y,Han Z. Key Engineering Materials . 2008
  • [2] Liu H K,Zeng R,Fu X K et al. Physica C Superconductivity and Its Applications . 1999
  • [3] M. Y. Li,Z. Han.The Effect of Lead-Rich Phases on Microstructure and Properties of (Bi, Pb)-2223/Ag Tapes. Superconductor Science and Technology . 2007
  • [4] Jiang J,Abell. Superconductor Science and Technology . 1997
  • [5] Masur L J,Kellers J,Li F et al. IEEE Transactions on Applied Superconductivity . 2002
  • [6] Chen X P,Grivel J C,Li M Y et al. Physica C Superconductivity and Its Applications . 2004
  • [7] E. Giannini,,E. Bellingeri,R. Passerini,and R. Flukiger."Direct observation of the Bi,Pb(2223) phase formation inside Ag-sheathed tapes and quantitative secondary phase analysis by means of in-situ high-temperature neutron diffraction,". Physica C Superconductivity and Its Applications . 1999
  • [8] Li M Y,Chen X P,Qu T M et al. Superconductor Science and Technology . 2004
  • [9] Li M Y,Chen X P,Qu T M et al. Superconductor Science and Technology . 2004
  • [10] Z. Han,P. Skov - Hansen,T. Fretoft,Supercond. Science and Technology . 1997
1