Effect of Different Surface Treatment Methods on the Friction and Wear Behavior of AISI 4140 Steel

被引：2

作者：

Mustafa Ulutan ^{[1
]}

Osman NCelik ^{[1
]}

Hakan Gasan ^{[2
]}

Umit Er ^{[1
]}

机构：

[1] University of Eskisehir Osmangazi,Faculty of Engineering,Department of Mechanical Engineering

[2] University of Eskisehir Osmangazi,Institute of Metallurgy

来源：

Journal of Materials Science & Technology | 2010年 / 26卷 / 03期

关键词：

AISI; 4140; steel; Quenching; Boronizing; Plasma transferred arc (PTA); Carburizing; Sliding wear;

D O I：

暂无

中图分类号：

TG142.15 [];

学科分类号：

080502 ;

摘要：

In this study,the effects of various surface treatments on the friction and wear behavior of AISI 4140 steel have been evaluated.Sample surfaces of AISI 4140 steel were treated by quenching,carburizing,boronizing and plasma transferred arc (PTA) modification.The microstructural characteristics of surface treated steel samples were examined by optical microscopy and scanning electron microscopy (SEM).The mechanical properties of the samples including the surface roughness,microhardness,and abrasive and adhesive wear characteristics were also evaluated.Wear tests were applied by using a block-on-disc configuration under dry sliding conditions.The wear behavior and friction characteristics of the samples were determined as a function of sliding distance.Each sample group was compared with the other sample groups,and it was observed that the carburized samples demonstrated the lowest weight losses;however,PTA-treated samples demonstrated the lowest coefficient of friction in comparison to the other sample groups at the same sliding distance.

引用

页码：251 / 257

页数：7

共 21 条

[1] WEAR [P].

CAILLIBOTTE MICHEL ;

ROUILLER VINCENT PHILIPPE .

日本专利 :JP2005226217A ,2005-08-25

[2]

S.H. Choo,,S. Lee,M.G. Golkovski. Materials Science and Engineering . 2000

[3]

A. Medina-Flores,J. Oseguera,P. Santiago,J.A. Ascencio. Surface and Coatings Technology . 2004

[4]

Y. Totik. Surface and Coatings Technology . 2006

[5]

S. Sen,U. Sen,C. Bindal. Materials Letters . 2006

[6]

F.E. Kennedy,D. Lidhagen,A. Erdemir,J.B. Wood- ford,T. Kato. Wear . 2003

[7]

T. Miokovi′c,V. Schulze,O. Vo¨hringer,D. Lo¨he. Acta Materialia . 2007

[8]

K. Padilla,A. Vela′squez,J.A. Berr′ os,E.S.P. Cabrera. Surface and Coatings Technology . 2002

[9]

K.H. Habig. Proc. of the Int. Conf. on Wear of Materials . 1983

[10]

A.G. Wang,I.M. Hutchings. Wear . 1988

← 1 2 3 →