Effect of Annealing Temperature on Magnetic Aftereffect and Positron Lifetime in Fe73.5Cu1Nb3Si13.5B9 Alloy

被引：0

作者：

Qixian BA

机构：

来源：

Journal of Materials Science & Technology | 2000年 / 04期

关键词：

Effect of Annealing Temperature on Magnetic Aftereffect and Positron Lifetime in Fe; B9; Alloy; Si;

D O I：

暂无

中图分类号：

TG111 [金属物理学];

学科分类号：

0702 ; 070205 ;

摘要：

The magnetic aftereffect （MAE） and the positron lifetime were measured at room temperature on the Fe73.5Cu1 Nb3Si13.5 B9 alloy in as-cast and after annealing at temperature Ta in the range from 450 to 750℃ It was found that both the MAE and the positron lifetime decrease with increasing Ta when T≤600℃. While Ta≥650℃, MAE is essentially suppressed, and two positron lifetimes appear.