Temperature Effect on Early Oxidation Behavior of NiCoCrAlY Coatings: Microstructure and Phase Transformation

被引：0
作者：
A. Ullah [1 ,2 ]
A. Khan [1 ,3 ]
Z. B. Bao [2 ]
Y. F. Yang [4 ]
M. M. Xu [2 ]
S. L. Zhu [2 ]
F. H. Wang [5 ]
机构：
[1] University of Chinese Academy of Sciences
[2] Shi-Changxu Innovation Center for Advanced Materials, Institute of Metal Research , Chinese Academy of Sciences
[3] Key Laboratory of Green Fabrication and Surface Technology of Advanced Metal Materials, Ministry of Education, School of Materials Science and Engineering , Anhui University of Technology
[4] Institute of Advanced Wear and Corrosion Resistant and Functional Material , Jinan University
[5] Shenyang National Laboratory for Materials Science , Northeastern University
来源：
ActaMetallurgicaSinica(EnglishLetters) | 2022年 / 35卷 / 06期
基金：
中国国家自然科学基金;
关键词：
D O I：
暂无
中图分类号：
TG174.4 [金属表面防护技术];
学科分类号：
080503 ;
摘要：
Initial oxidation behavior of NiCoCrAlY coating prepared by arc-ion plating has been studied in air at 900, 1000 and 1100 °C. The results showed that phase transformation from transient θ-Al2O3to α-Al2O3was highly related to the temperature and oxidation time. The oxide scale in the initial stage was mainly composed of θ-Al2O3at 900 °C. Instead, more amount of α-Al2O3emerged out with increasing oxidation temperature. The elemental distribution after oxidation confirmed that faster chromium diffusion to the oxide scale played an important role in the speedy transformation from θ-Al2O3to α-Al2O3. Y segregation at scale/coating interface resulted in less cavity formation and hence improved the oxide scale adherence.
引用
收藏
页码：975 / 984
页数：10
相关论文
共 50 条
  • [1] Temperature Effect on Early Oxidation Behavior of NiCoCrAlY Coatings: Microstructure and Phase Transformation
    A. Ullah
    A. Khan
    Z. B. Bao
    Y. F. Yang
    M. M. Xu
    S. L. Zhu
    F. H. Wang
    Acta Metallurgica Sinica (English Letters), 2022, 35 : 975 - 984
  • [2] Temperature Effect on Early Oxidation Behavior of NiCoCrAlY Coatings: Microstructure and Phase Transformation
    Ullah, A.
    Khan, A.
    Bao, Z. B.
    Yang, Y. F.
    Xu, M. M.
    Zhu, S. L.
    Wang, F. H.
    ACTA METALLURGICA SINICA-ENGLISH LETTERS, 2022, 35 (06) : 975 - 984
  • [3] Effect of vacuum annealing on initial oxidation behavior and alumina transition of NiCoCrAlY coatings
    Ullah, A.
    Khan, A.
    Bao, Z. B.
    Yu, C. T.
    Zhu, S. L.
    Wang, F. H.
    SURFACE & COATINGS TECHNOLOGY, 2020, 404
  • [4] Effect of Mo on microstructure and oxidation of NiCoCrAlY coatings on high Nb containing TiAl alloys
    Gong, X.
    Chen, R. R.
    Yang, Y. H.
    Wang, Y.
    Ding, H. S.
    Guo, J. J.
    Su, Y. Q.
    Fu, H. Z.
    APPLIED SURFACE SCIENCE, 2018, 431 : 81 - 92
  • [5] Thermal stability and oxidation behavior of nanostructured NiCoCrAlY coatings
    Mercier, Dominic
    Gauntt, Bryan D.
    Brochu, Mathieu
    SURFACE & COATINGS TECHNOLOGY, 2011, 205 (17-18) : 4162 - 4168
  • [6] Effect of microstructure on early oxidation of MCrAlY coatings
    Chen, Ying
    Zhao, Xiaofeng
    Xiao, Ping
    ACTA MATERIALIA, 2018, 159 : 150 - 162
  • [7] Microstructure and oxidation resistance of nanometer SiC particles reinforced NiCoCrAlY coatings
    Wang, Hong-Yu
    Zuo, Dun-Wen
    Li, Xiang-Feng
    Yu, Ya-Ping
    Jiang, Yan
    Cailiao Kexue yu Gongyi/Material Science and Technology, 2010, 18 (06): : 847 - 851
  • [8] Isothermal oxidation behavior of HVAF-sprayed NiCoCrAlY coatings
    Bobzin, K.
    Heinemann, H.
    Jasutyn, K.
    Tan, C.
    SURFACE & COATINGS TECHNOLOGY, 2025, 498
  • [9] The effect of yttrium content on the oxidation-induced degradation of NiCoCrAlY coatings and the influence of surface roughness on the oxidation of NiCoCrAlY and platinum aluminide coatings
    Yanar, N. M.
    Meier, E. M.
    Pettit, F. S.
    Meier, G. H.
    MATERIALS AT HIGH TEMPERATURES, 2009, 26 (03) : 331 - 338
  • [10] High temperature damping behavior of plasma sprayed NiCoCrAlY coatings
    Khor, KA
    Chia, CT
    Gu, YW
    Boey, FYC
    JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2002, 11 (03) : 359 - 364
12345