Effects of Sc, Zr and Tion the microstructure and properties of Al alloys with high Mg content

被引：0

作者：

WANG Xu CHEN Guoqin LI Bing WU Lianmei and JIANG Daming School of Materials Science and Engineering Harbin Institute of Technology Harbin China ^{[150001
]}

机构：

来源：

RareMetals | 2010年 / 29卷 / 01期

关键词：

Al-Mg alloy; homogenization; microstructure; Brinell hardness; element addition;

D O I：

暂无

中图分类号：

TG146.21 [];

学科分类号：

080502 ;

摘要：

The effects of trace Sc, Zr, and Ti on the microstructure and hardness of Al alloys with high Mg content (Al-6Mg, Al-8Mg, and Al-10Mg) were studied by optical microscope, scanning electron microscopy (SEM), transmission electron microscopy (TEM), and Brinell hardness. The grain size of the ascast alloys was refined by the addition of Sc and Zr, and it was further refined by the addition of Ti. With the same contents of Sc, Zr, and Ti, an increase in Mg content was beneficial to the refinement due to the solution of Mg into α-Al. The refined microstructures of the as-cast alloys were favorable for Brinell hardness. Addition of Sc, Zr, and Ti to the Al-10Mg alloy results in the improvement of peak hardness and it is about 45% higher than that of the Al-10Mg alloy, which is due to fine precipitations of Al3(Sc1-xZrx), Al3(Sc1-xTix), and Al3(Sc1-x-yZrxTiy).

引用

页码：66 / 71

页数：6

共 12 条

[1]

Effect of Sc on Precipitation Hardening of AlSi6Mg Alloy[J]. Wattanachai Prukkanon,Satit Chanpum,Chaowalit Limmaneevichitr.Journal of Materials Science ＆ Technology. 2008(01)

[2]

Effect of homogenization treatment on microstructure and properties of Al-Mg-Mn-Sc-Zr alloy[J]. 聂波,尹志民,朱大鹏,彭勇宜,姜锋,黄继武.Journal of Central South University of Technology. 2007(04)

[3] Effect of Scandium Additions on the Tensile Properties of Cast Al-6Mg alloys [J].

Kaiser, M. S. ;

Datta, S. ;

Roychowdhury, A. ;

Banerjee, M. K. .

JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2008, 17 (06) :902-907

[4]

Microstructure, mechanical properties and corrosion behaviour of dilute Al–Sc–Zr alloy prepared by powder metallurgy[J] . V. Neubert,B. Smola,I. Stulíková,A. Bakkar,J. Reuter.Materials Science ＆ Engineering A . 2007 (1)

[5]

A cast 7050 friction stir weld with scandium: microstructure, corrosion and environmental assisted cracking[J] . C.S. Paglia,K.V. Jata,R.G. Buchheit.Materials Science ＆ Engineering A . 2006 (1)

[6]

Optimization of hardening of Al–Zr–Sc cast alloys[J] . N. A. Belov,A. N. Alabin,D. G. Eskin,V. V. Istomin-Kastrovskii.Journal of Materials Science . 2006 (18)

[7] Microstructure and age hardening response of cast Al-Mg-Sc-Zr alloys [J].

Singh, V ;

Prasad, KS ;

Gokhale, AA .

JOURNAL OF MATERIALS SCIENCE, 2004, 39 (08) :2861-2864

[8]

Mechanical properties of Al（Sc,Zr） alloys at ambient and elevated temperatures[J] . Christian B. Fuller,David N. Seidman,David C. Dunand.Acta Materialia . 2003 (16)

[9]

Effect of minor Sc and Zr on the microstructure and mechanical properties of Al–Mg based alloys[J] . Zhimin Yin,Qinglin Pan,Yonghong Zhang,Feng Jiang.Materials Science ＆ Engineering A . 2000 (1)

[10]

Fatigue properties of Al-Mg alloys with and without scandium[J] . O. Roder,T. Wirtz,A. Gysler,G. Lütjering.Materials Science ＆ Engineering A . 1997

← 1 2 →