Corrosion behavior of coating with plasma sprayed 8YSZ on the surface of carbon steel

被引：0
|
作者：
刘扬佳 [1 ]
范习之 [1 ]
曾水冰 [1 ]
王盈 [2 ]
邹兵林 [2 ]
古立建 [2 ]
陈小龙 [2 ]
Zuhair Subhani Khan [2 ]
杨道武 [1 ]
曹学强 [1 ,2 ]
机构：
[1] Department of Chemical and Biological Engineering,Changsha University of Science and Technology
[2] State Key Laboratory of Rare Earth Resources Utilization,Changchun Institute of Applied Chemistry,Chinese Academy of Sciences
来源：
JournalofRareEarths | 2012年 / 30卷 / 06期
基金：
中国国家自然科学基金;
关键词：
thermal barrier coating; carbon steel; corrosion behavior; electrochemical impedance spectroscopy; rare earths;
D O I：
暂无
中图分类号：
TG174.44 [金属复层保护];
学科分类号：
080503 ;
摘要：
The corrosion behavior of plasma sprayed 8YSZ(ZrO2 stabilized by 8 wt.%Y2O3)coating on the surface of carbon steel in seawater was investigated.The electrochemical impedance spectroscopy was used as a non-destructive evaluation technique to monitor the protection properties of the coating when it was immersed in seawater,and corrosion products were characterized by scanning electron microscopy,energy dispersive spectrometry and X-ray photoelectron spectroscopy.The results indicated that three time constants were obtained during the initial immersion period,and then a new time constant appeared due to the formation of rust layer,which was corresponding to the corrosion process.Corrosion products were formed on the coating surface as well as inside the coating,and the crystalline composition of the rust layer mainly consisted of γ-FeOOH.
引用
收藏
页码：592 / 598
页数：7
相关论文
共 50 条
  • [1] Corrosion behavior of coating with plasma sprayed 8YSZ on the surface of carbon steel
    Liu Yangjia
    Fan Xizhi
    Zeng Shuibing
    Wang Ying
    Zou Binglin
    Gu Lijian
    Chen Xiaolong
    Khan, Zuhair Subhani
    Yang Daowu
    Cao Xueqiang
    JOURNAL OF RARE EARTHS, 2012, 30 (06) : 592 - 598
  • [2] Effect of Laser Alloying TiC Doping on the Hot Corrosion Behavior of Plasma Sprayed 8YSZ Thermal Barrier Coatings
    Zhang, Panpan
    Sun, Yuhai
    Sun, Lei
    Li, Bo
    Zhang, Qunli
    Yao, Jianhua
    CHINA SURFACE ENGINEERING, 2023, 36 (06) : 126 - 134
  • [3] Thermal shock behavior of a 8YSZ/CoCrAlYTaSi thermal sprayed barrier coating on GH202 superalloy
    Cao, Jiangdong
    Gao, Keke
    Cao, Xue Yu
    Jiang, Bocheng
    CERAMICS INTERNATIONAL, 2020, 46 (06) : 7489 - 7498
  • [4] Rule of Influence of Stress Relief Groovefor Residual Stress of Plasma Sprayed Mo/8YSZ Thermal Barrier Coating
    Zhang X.
    Pang M.
    Jiang G.
    Pang, Ming (pangming1980@126.com), 1600, Editorial Office of Chinese Rare Earths (38): : 521 - 531
  • [5] Effect of Cooling Modes on Residual Stress of Plasma Sprayed Mo/8YSZ Thermal Barrier Coatings
    Cui Y.
    Zhang X.
    Pang M.
    Zhongguo Xitu Xuebao/Journal of the Chinese Rare Earth Society, 2020, 38 (02): : 196 - 207
  • [6] Hot Corrosion Resistance of 8YSZ Thermal Barrier Coating Modified by Laser Alloying
    Sun Lei
    Guo Yujia
    Zhang Panpan
    Rong, Liu
    Zhang Qunli
    Yao Jianhua
    CHINESE JOURNAL OF LASERS-ZHONGGUO JIGUANG, 2023, 50 (04):
  • [7] Cracking Behavior of Atmospheric Plasma-Sprayed 8YSZ Thermal Barrier Coatings during Thermal Shock Test
    Huang, Jibo
    Sun, Wen
    Huang, Renzhong
    Ma, Wenhua
    COATINGS, 2023, 13 (02)
  • [8] Hot corrosion behaviour of plasma sprayed alumina + YSZ particle composite coating
    Muhammet Karabaş
    Emre Bal
    Yılmaz Taptik
    Protection of Metals and Physical Chemistry of Surfaces, 2017, 53 : 859 - 863
  • [9] Influence Rule of Different Ratios of Gradient Layer on Residual Stress of Plasma Sprayed Mo/8YSZ Functionally Graded Thermal Barrier Coating
    Pang M.
    Liu Q.
    Zhang X.
    Zhongguo Xitu Xuebao/Journal of the Chinese Rare Earth Society, 2020, 38 (05): : 677 - 687
  • [10] Hot corrosion behaviour of plasma sprayed alumina plus YSZ particle composite coating
    Karabas, Muhammet
    Bal, Emre
    Taptik, Yilmaz
    PROTECTION OF METALS AND PHYSICAL CHEMISTRY OF SURFACES, 2017, 53 (05) : 859 - 863
12345