WC-M coating to improve resistance of hydraulic turbines to cavitation erosion and abrasion

被引：0

作者：

王飚

王宇东

张自华

机构：

[1] DepartmentofMechanicalEngineering,DepartmentofMechanicalEngineering,DepartmentofMechanicalEngineeringKunmingUniversityofScienceandTechnology,Kunming,China,KunmingUniversityofScienceandTechnology,Kunming,China,KunmingUniversityofScienceandTechnology,Kunming

来源：

Transactions of Nonferrous Metals Society of China | 2003年 / 04期

关键词：

WC M coating; cavitation erosion; abrasion hydraulic turbines;

D O I：

暂无

中图分类号：

TG174.44 [金属复层保护];

学科分类号：

080503 ;

摘要：

WC M hard faced ceramic coating was made on the substrate of steel by means of high velocity oxygen fuel flame (HVOF) thermal spraying. The resistance of this coating to cavitation erosion and abrasion (CEA) is about 2.5 times higher than that of 188 stainless steel, and is about 1.5 times higher than that of Stellite alloy (CoCrWC) made in America. When this coating were applied to the hydraulic power stations with more silt content in the flow water, which reaches 50 kg/m 3, the resistance of above mentioned coating to CEA was about 2 times to that of NiCr alloy coating, and is about 45 times to that of OCr13Ni4Mo stainless steel. In addition, the micro hardness, microstructures and electron probe analyzing of the WC M coating are all discussed.

引用

页码：893 / 897

页数：5

共 13 条

[1]

Preparing method of alloys to resist wear. Mazmu L,Kabada K,Kouzikai T,et al. . 1992

[2] WEAR [P].

UEDA SHIGEAKI .

日本专利 :JPH07300705A ,1995-11-14

[3]

Microstructure of interface between HVOF sprayed WC-CO coating and spring steel substrate. SHAO Bei-ling,LUI An-sheng,WANG Xiao-hua,et al. Transactions of Nonferrous Metals Society of China . 1996

[4]

Erosion and cavitation corrosion resistance of nickel-based coating. KANG Jin-xing,ZHAO Wen-zheng. Materials Protection . 2002

[5]

Erosion and cavitation corrosion resistance of nickel-based coating. KANG Jin-xing,ZHAO Wen-zheng. Materials Protection . 2002

[6]

Advances of the coatings of hydraulic turbines to resist erosion. CHENG Shao-ping. Machines of Hydraulic and Power . 1997

[7]

Thermal Spraying Method. Sokol L,Beach D,Fla N,et al. . 1995

[8]

A study of HVOF thermally sprayed tungsten carbide based coating. Verdon C,Karimi A,Martin J. Journal of Materials Science . 1998

[9]

Corrosion resistance of laser clad Ni base alloys. ZHOU Rong,ZHANG Xiao-bao,SI Yun-sen. The Chinese Journal of Nonferrous Metals . 1999

[10]

Optimization design of metallic materials to resist cavitation erosion and abrasion. WANG Biao,ZHANG Zi-hua,WANG Ye-dong. Engineering Science of China . 2000

← 1 2 →