Rolling route for refining grains of super light Mg-Li alloys containing Sc and Be

被引：0

作者：

CHIANG Chih-Te

LEE Shyong

机构：

[1] DepartmentofMechanicalEngineering,NationalCentralUniversity

来源：

Transactions of Nonferrous Metals Society of China | 2010年 / 20卷 / 08期

关键词：

Mg-Li alloy; beryllium; scandium; solid solution strengthening;

D O I：

暂无

中图分类号：

TG339 [有色金属轧制];

学科分类号：

080201 ; 080503 ;

摘要：

Pioneering work on Sc or/and Be added Mg-Li alloys with refined grains was initiated.Various rolling-based thermo-mechanical treatments on these Mg-Li alloys were carried out.Four Mg-Li alloys were prepared by vacuum melting process.A unique route for producing fine grains was applied which concluded solution treatment at 350°C,cold rolling with 60% thickness reduction and 250°C annealing,successively.

引用

页码：1374 / 1379

页数：6

共 7 条

[1] MICROSTRUCTURE AND MECHANICAL PROPERTIES OF Mg-Li ALLOY WITH Ca ADDITION [J].

HB Li GC Yao ZQ Guo YH Liu HJ Yu and HB Ji School of Materials Metallurgy Northeastern University Shenyang China .

Acta Metallurgica Sinica(English Letters), 2006, (05) :355-361

[2]

Ultrafine-grained Mg–9Li–1Zn alloy sheets exhibiting low temperature superplasticity[J] . W.J. Kim,M.J. Kim,J.Y. Wang.Materials Science ＆ Engineering A . 2009 (1)

[3]

Microstructure evolution of Mg–14% Li–1% Al alloy during the process of equal channel angular pressing[J] . T. Liu,S.D. Wu,S.X. Li,P.J. Li.Materials Science ＆ Engineering A . 2007

[4]

Superplasticity evaluation in an extruded Mg–8.5Li alloy[J] . ShangLi Dong,Tsunemichi Imai,Suk-Won Lim,Naoyuki Kanetake,Naobumi Saito.Journal of Materials Science . 2007 (13)

[5]

Flow and cavitation in a quasi-superplastic two-phase magnesium–lithium alloy[J] . Megumi Kawasaki,Kohei Kubota,Kenji Higashi,Terence G. Langdon.Materials Science ＆ Engineering A . 2006 (1)

[6]

Improving the superplastic properties of a two-phase Mg–8% Li alloy through processing by ECAP[J] . Mitsuaki Furui,Cheng Xu,Tetsuo Aida,Makoto Inoue,Hiroshi Anada,Terence G. Langdon.Materials Science ＆ Engineering A . 2005

[7]

Characteristics of superplasticity domain in the processing map for hot working of as-cast Mg–11.5Li–1.5Al alloy[J] . O Sivakesavam,Y.V.R.K Prasad.Materials Science ＆ Engineering A . 2002 (1)

← 1 →