Effects of P addition on the microstructure and mechanical properties of Mg–5%Sn–1.25%Si alloy

The effects of Al-P addition on the microstructure and mechanical properties of as-cast Mg–5%Sn–1.25%Si magnesium alloy were investigated. The results show that the phases of the as-cast alloy are composed of α-Mg, Mg2 Sn, Mg2 Si, little P, and AlP. The Chinese character shape Mg2 Si phase changes into a granular morphology by P addition because AlP can act as a heterogeneous nucleation core for the Mg2 Si phase. When 0.225wt% of Al–3.5%P alloy is added, the mechanical properties of the Mg–5%Sn–1.25%Si alloy are greatly improved, and the tensile strength increases from 156 to 191 MPa, an increase of 22.4% compared to the alloy without P addition. When the amount of Al–3.5%P reaches 0.300wt%, a segregation phenomenon occurs in the granular Mg2 Si phase, and the tensile strength and hardness decrease though the elongation increases.