Regulatable pervaporation performance of Zn-MOFs/polydimethylsiloxane mixed matrix pervaporation membranes

Pervaporation(PV) is an emerging separation technique for liquid mixture. Mixed matrix membranes(MMMs) often demonstrate trade-off relationship between separation factor and flux. In this study, by changing the organic linkers(2-methyl imidazolate, imidazole-2-carboxaldehyde, 2-ethyl imidazolate),ZIF-8, ZIF-90 and MAF-6 were prepared and filled in polydimethylsiloxane(PDMS) membranes for dealcoholization of 5%(mass) n-butanol solution, and the membranes properties and pervaporation performances were adjusted. Compared with the pure PDMS membrane, the addition of ZIF-8 resulted in a 9% increase in flux(1136 g·m-2·h-1) and a 22.5% increase in separation factor(28.3), displaying antitrade-off effect. For the MAF-6/PDMS MMMs(2.0% mass loading), the pervaporation separation index(PSI) and separation factor were 32347 g·m-2·h-1and 58.6 respectively(increased by 34% and 154% in contrast with that of the pure PDMS membrane), and the corresponding permeation flux was 552 g·m-2·h-1, presenting great potential in the removal butanol from water. It was deduced that the large aperture size combined with moderate hydrophobicity of metal–organic frameworks(MOFs) favor the concurrent increase in permeability and selectivity.