Effect of heat treatment on microstructures and properties of a novel Al-Zn-Mg-Cu alloy for oil drilling

In view of the special requirements for strength, heat resistance and corrosion resistance of Al-Zn-Mg-Cu alloy for oil drilling, the Al-6.2 Zn-2.5 Mg-1.6 Cu alloy was prepared by increasing Cu content on basis of Russian Series 1953 alloy. The effect of heat treatment on the microstructures and properties of the alloy was characterized by optical microscope（OM）, scanning electron microscope（SEM） and transmission electron microscope（TEM）, and investigated by tensile test at room temperature, thermal exposure test and corrosion test. The results show that the strength after T6 aging treatment exhibit a decrease trend as an increase of the solution temperature from465 °C to 480 °C. After the solution treated by the rate of 470 °C/1 h, second phases dissolve into the matrix very well and the strength property reaches optimum. The alloy has better comprehensive properties treated by a solution treatment of 470 °C/1 h and then followed by an aging treatment of 120 °C/24 h + 170 °C/1 h + 120 °C/24 h. Under the aging state, the precipitated phases inside the grains are suitable in size, while on the grain boundary distribute discontinuously and the precipitate-free zone is obvious. Besides, the alloy still maintain high tensile properties. The yield strength, tensile strength and elongation are 650 MPa, 686 MPa,12.0%, respectively. The yield strength retention after heat exposure is 92%. The alloy has good corrosion resistance and the exfoliation corrosion degree. The average corrosion rate in the H;S and CO;environment is 0.0024 mm/a, which is far less than the required 0.12 mm/a. It is insensitive to H;S and CO;environments.