MicrostructureandPropertiesofFe-12Cr-2.5W-xSi-0.4Ti-0.3Y2O3Alloys

被引：0

作者：

孙魁

姚振华

WANG Chaofeng

DU Xueming

机构：

[1] SchoolofMaterialsScienceandEngineer,WuhanUniversityofTechnology

来源：

JournalofWuhanUniversityofTechnology(MaterialsScience) | 2023年 / 38卷 / 04期

关键词：

D O I：

暂无

中图分类号：

TG141 [黑色金属材料];

学科分类号：

080502 ;

摘要：

Fe-12Cr-2.5W-x Si-0.4Ti-0.3Y2O3 alloys were fabricated by mechanical alloying and vacuum sintering. The effect of sintering temperature and Si content on the microstructure and properties of the alloy was investigated systematically. The experimental results show that the relative density and tensile strength of the alloy were increased with the elevating of sintering temperature and Si content within a certain range.The alloy with 1wt% Si sintered at 1 350 ℃ exhibited superior properties, and the relative density and tensile strength were 96.8% and 692.7 MPa, respectively. HAADF and EDAX analysis of nano-precipitation in the matrix indicated that Si could combine with Y, Ti, and O in the sintering process, which was uniformly distributed with the size of 10 nm. Portion of Y2O3 had not completely dissolved in the milling process, which was retained in the matrix of the alloy.

引用

页码：893 / 896

页数：4

共 15 条

[1] Microstructure and Mechanical Properties of AZ31 Alloys Processed by Residual Heat Rolling [J].

刘杨 ;

ZHAO Yiquan ;

王岭 ;

JIN Xiuying ;

SUN Chao ;

WANG Xiaomin ;

WANG Gang ;

DAI Shiyu ;

WANG Yinong .

JournalofWuhanUniversityofTechnology(MaterialsScience), 2021, 36 (04) :588-594

[2]

S. Rogozhkin,A. Bogachev,O. Korchuganova,A. Nikitin,N. Orlov,A. Aleev,A. Zaluzhnyi,M. Kozodaev,T. Kulevoy,B. Chalykh,R. Lindau,J. Hoffmann,A. M?slang,P. Vladimirov,M. Klimenkov,M. Heilmaier,J. Wagner,S. Seils.Nanostructure evolution in ODS steels under ion irradiation[J].Nuclear Materials and Energy,2016(C)

[3] Advanced TEM characterization of oxide nanoparticles in ODS Fe–12Cr–5Al alloys [J].

Kinga A. Unocic ;

Bruce A. Pint ;

David T. Hoelzer .

Journal of Materials Science, 2016, 51 :9190-9206

[4]

E. Gil,N. Ordás,C. García-Rosales,I. Iturriza.Microstructural characterization of ODS ferritic steels at different processing stages[J].Fusion Engineering and Design,2015

[5]

Z. Oksiuta,A. Ozieblo,K. Perkowski,M. Osuchowski,M. Lewandowska.Influence of HIP pressure on tensile properties of a 14Cr ODS ferritic steel[J].Fusion Engineering and Design,2014

[6]

J. D. Bolton,M. Jeandin,C. Jouanny Trésy.Mechanisms of Sintering in High Speed Steels with Phosphorus Alloying Additions[J].Powder Metallurgy,2013(2)

[7]

Xiu Lin,Mingwei Li,Yesheng Zhong,Yijie Zhao,Yue Sun,Shuyuan Zhao,Xiaodong He.Microstructure and hardness of nanocrystalline ferritic ODS alloy foil with high oxide content fabricated by EBPVD[J].Applied Surface Science,2013

[8] Microstructural evolution of oxide-dispersion-strengthened Fe–Cr model steels during mechanical milling and subsequent hot pressing [J].

Lei Dai ;

Yongchang Liu ;

Zongqing Ma ;

Zhizhong Dong ;

Liming Yu .

Journal of Materials Science, 2013, 48 :1826-1836

[9]

H. Xing,J. Sun,J. Huang,Z.J. Zhou.Structure and elastic property of nanosized complex oxide particles in ferritic/martensitic alloy: An electron energy-loss spectroscopy study[J].Journal of Nuclear Materials,2011(3)

[10] Relation between microstructure and Charpy impact properties of an elemental and pre-alloyed 14Cr ODS ferritic steel powder after hot isostatic pressing [J].

Oksiuta, Z. ;

Boehm-Courjault, E. ;

Baluc, N. .

JOURNAL OF MATERIALS SCIENCE, 2010, 45 (14) :3921-3930

← 1 2 →