Laser Quenching and Ion Sulphidizing Complex Surface Treat Technology for Diesel Engine Cylinder

被引:1
作者
谢兆钱 [1 ]
机构
[1] Northwest Institute of Nuclear Technology
基金
中国国家自然科学基金;
关键词
cylinder; laser quenching; ion sulphidizing; friction and wear;
D O I
暂无
中图分类号
TG174.4 [金属表面防护技术];
学科分类号
080503 ;
摘要
In order to solve the problem of wear-out-failure of diesel engine cylinder, the laser-quenching and low temperature ion sulfurizing complex surface treatment technology was operated on the surface of 42MnCr52 steel. And the tribological properties of the complex layer were investigated. The experimental results indicated that the complex layer was composed of soft surface sulphide layer and sub-surface laser-quenching harden layer, and showed excellent friction-reduction and wear-resistance performance at high temperature. The synergistic effect of the complex layer resulted in 20% increase in hardness, 10% reduction in friction coefficient and 50% reduction in wear weight loss, respectively, compared with those of the standard samples. The bench-test further demonstrated that this technology can improve the lubricating condition between cylinder and piston ring, and reduce both abnormity wear when the lubricating oil is deficiency at the time of start-up and sticking wear at high temperature during the operating period, and then prolong the service life of engine.
引用
收藏
页码:1115 / 1119
页数:5
相关论文
共 7 条
  • [1] 渗硫层对网格化激光淬火表面摩擦磨损性能的影响
    乔玉林
    赵玉强
    刘晓亭
    杨善林
    [J]. 装甲兵工程学院学报, 2010, 24 (05) : 73 - 77
  • [2] Optimization of Laser Ablation Technology for PDPhSM Matrix Nanocomposite Thin Film by Artificial Neural Networks-particle Swarm Algorithm[J]. 唐普洪,宋仁国. Journal of Wuhan University of Technology(Materials Science Edition). 2010(02)
  • [3] Wear Performance of Laser Surface Hardened GCr15 Steel[J]. 雷声. Journal of Wuhan University of Technology(Materials Science Edition). 2010(01)
  • [5] 离子渗硫技术在装甲车辆中的应用
    赵军军
    张平
    韩文政
    [J]. 装甲兵工程学院学报, 2003, (01) : 13 - 17
  • [6] The prediction of the mechanical properties of metal during laser quenching[J] . Y.H. Guan,T.L. Chen,H.G. Wang,J.T. Zhang. Journal of Materials Processing Tech. . 1997 (1)
  • [7] Spectroscopic properties and quenching processes of Yb3+ in Fluoride single crystals for laser applications .2 A. Bensalah,M. Ito,Y. Guyot,C. Goutaudier,A. Jouini,A. Brenier,H. Sato,T. Fukuda,G. Boulon. J. Lumin . 2007