Microstructure evolution of semi-solid Mg-14Al-0.5Mn alloys during isothermal heat treatment

A new Mg-14Al-0.5Mn alloy that exhibits a wide solidification range and sufficient fluidity for semi-solid forming was designed.And the microstructure evolution of semi-solid Mg-14Al-0.5Mn alloy during isothermal heat treatment was investigated. The mechanism of the microstructure evolution and the processing conditions for isothermal heat treatment were also discussed.The results show that the microstructures of cast alloys consist ofα-Mg,β-Mg17Al12 and a small amount of Al-Mn compounds.After holding at 520℃ for 3 min,the phases ofβ-Mg17Al12 and eutectic mixtures in the Mg-14Al-0.5Mn alloy melt and the microstructures ofα-Mg change from developed dendrites to irregular solid particles.With increasing the isothermal time,the amount of liquid increases,and the solid particles grow large and become spherical.When the holding time lasts for 20 min or even longer,the solid and liquid phases achieve a state of dynamic equilibrium.