Hot deformation mechanism and microstructure evolution of TC11 titanium alloy in β field

被引：0

作者：

陈慧琴 ^{[1
,2
]}

曹春晓 ^{[1
]}

郭灵 ^{[1
]}

林海 ^{[1
]}

机构：

[1] Beijing Institute of Aeronautical Materials

[2] School of Materials Science and Engineering,Taiyuan University of Science and Technology

来源：

Transactions of Nonferrous Metals Society of China | 2008年 / 05期

关键词：

TC11 titanium alloy; hot deformation; microstructure evolution;

D O I：

暂无

中图分类号：

TG146.23 [];

学科分类号：

080502 ;

摘要：

Hot deformation behaviors of TC11 alloy with β-annealed lamellar structure and forged equiaxed structure were investigated in the β field in the temperature range of 1 090-1 030 ℃ and strain rate of 0.001-0.1 s-1 by means of isothermal compression tests.Hot deformation characteristics and microstructure evolutions of the two starting structures were analyzed.And hot processing power dissipation efficiency maps were established.EBSD technique was used for testing grain boundary characteristic of deformation structures.The results indicate that hot deformation mechanism of TC11 alloy in β field is dynamic recovery accompanied by geometric dynamic recrystallization at large strains,or discontinuous dynamic recrystallization based on the starting structure states and deformation parameters.Accordingly,there are two different grain refining patterns.One is characteristic of new fine grains in the interior of elongated prior β grains that have serrated grain boundaries; and the other is that of new fine grains along elongated prior β grain boundaries.

引用

页码：1021 / 1027

页数：7

共 4 条

[1]

Geometric Dynamic Recrystallization in α-Zirconium at Elevated Temperatures[J] . Barrabes S.R.,Kassner M.E.,Pérez-Prado Maria Teresa,Evangelista E..Materials Science Forum . 2004 (467)

[2]

Geometric Dynamic Recrystallization in an AA2219 Alloy Deformed to Large Strains at an Elevated Temperature[J] . Kaibyshev Rustam,Mazurina I.,Sitdikov Oleg.Materials Science Forum . 2004 (467)

[3]

Effect of preform microstructure on the hot working mechanisms in ELI grade Ti–6Al–4V: transformed β v . equiaxed （ α + β ）[J] . Prasad,Seshacharyulu,Medeiros,Frazier.Materials Science and Technology . 2000 (5)

[4]

Hot deformation mechanisms in ELI Grade Ti-6a1-4V[J] . T. Seshacharyulu,S.C. Medeiros,J.T. Morgan,J.C. Malas,W.G. Frazier,Y.V.R.K. Prasad.Scripta Materialia . 1999 (3)

← 1 →