CorrosionbehaviorofaluminumalloysinNa2SO4solutionusingthescanningelectrochemicalmicroscopytechnique

被引：0
作者：
Herong Zhou Xiaogang Li Chaofang Dong Kui Xiao and Tai Li School of Materials Science and EngineeringUniversity of Science and Technology BeijingBeijing China Beijing Key Laboratory for CorrosionErosion and Surface TechnologyBeijing China [1 ,2 ,1 ,2 ,1 ,1 ,1 ,1 ,100083 ,2 ,100083 ]
机构：
来源：
InternationalJournalofMineralsMetallurgyandMaterials | 2009年 / 15卷 / 01期
关键词：
aluminum alloys; corrosion behavior; intermetallic particles; scanning electrochemical microscopy(SECM);
D O I：
暂无
中图分类号：
TG172 [各种类型的金属腐蚀];
学科分类号：
080503 ;
摘要：
The corrosion behavior of aluminum alloys 1060 and 2A12 in a 10 mM Na2SO4+5 mM KI solution was investigated by scanning electrochemical microscopy(SECM) and scanning electron microscopy(SEM) . The potential topography and corrosion morphology results show that the potential of the sample surface over the same area changes with the increase of immersion time. The corrosion area becomes large,and the potential becomes more negative. The corrosion potential of the 2A12 alloy surface is lower than that of 1060 aluminum,and 2A12 alloy becomes easily corrosive. This is the reason that preferential dissolution in the boundary region of some intermetallic particles(IMPs) occurs and different dissolution behaviors are associated with different types of IMPs because of different potentials.
引用
收藏
页码：84 / 88
页数：5
相关论文
共 50 条
[31]   Corrosion behavior of Ni3Al-bonded TiC-based cermets in H2SO4 and NaOH solutions [J].
Mao, Qiao ;
Yang, Qingqing ;
Xiong, Weihao ;
Li, Shengtao ;
Zhang, Man ;
Ruan, Linji .
CERAMICS INTERNATIONAL, 2018, 44 (11) :13303-13312
[32]   Corrosion behavior and biocompatibility of hydroxyapatite coating on H2SO4 passivated 316L SS for human body implant [J].
Ali Parsapour ;
Saied Nouri Khorasani ;
Mohammad Hossein Fathi .
Acta Metallurgica Sinica (English Letters), 2013, 26 :409-415
[33]   Corrosion behavior of micro-arc oxidation coating on magnesium alloy AZ91D in Na2SO4 solution [J].
Guo, Huixia ;
Ma, Ying ;
Zhang, Yufu ;
Dong, Hairong ;
Hao, Yuan .
Kuei Suan Jen Hsueh Pao/Journal of the Chinese Ceramic Society, 2013, 41 (03) :382-387
[34]   Hydrogen absorption in solution/mill annealed Alloy 600 at room temperature H2SO4 and high-temperature pressurized water [J].
Arjmand, Farzin ;
Zhao, Zhengjie ;
Guan, Kaishu ;
Zhang, Lefu .
CORROSION SCIENCE, 2022, 198
[35]   Dissolution and repair of passive film on Cu-bearing 304L stainless steels immersed in H2SO4 solution [J].
Zhang, Xinrui ;
Zhao, Jinlong ;
Xi, Tong ;
Shahzad, M. Babar ;
Yang, Chunguang ;
Yang, Ke .
JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2018, 34 (11) :2149-2159
[36]   Corrosion behavior of precracked SiCf/SiC composites under 1200-1300°C Na2SO4-wet-oxygen environment [J].
Guo, Feiyu ;
Chen, Xiaowu ;
Zhang, Junmin ;
Yang, Jinshan ;
Zhang, Xiangyu ;
Kan, Yanmei ;
Xue, Yudong ;
Qin, Hao ;
Dong, Shaoming .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2024, 107 (06) :3701-3715
[37]   Friction and wear behaviour of selected titanium and zirconium based nitride coatings in Na2SO4 aqueous solution under low contact pressure [J].
Pejakovic, Vladimir ;
Totolin, Vladimir ;
Goecerler, Hakan ;
Brenner, Josef ;
Ripoll, Manel Rodriguez .
TRIBOLOGY INTERNATIONAL, 2015, 91 :267-273
[38]   Electrochemical and XPS studies of a Nb-containing Ti-based glass-forming alloy system in H2SO4 solution [J].
Cheng, Xiang ;
Huang, YongJiang ;
Zhou, BinJun ;
Xue, Peng ;
Fan, HongBo ;
Sun, JianFei .
ELECTROCHEMISTRY COMMUNICATIONS, 2015, 60 :139-143
[39]   Electrochemical and surface characteristics of sputter-deposited amorphous Mn-Zr-Cr alloys in a 1 M H2SO4 solution [J].
El-Moneim, A. A. ;
Ezzat, M. ;
Badawy, W. A. .
RSC ADVANCES, 2015, 5 (31) :24460-24468
[40]   Investigation of Anodic Behavior of Nickel in H2SO4 Solutions Using Galvanostatic Polarization Technique. I. Kinetics and Thermodynamic Approach [J].
Wanees, S. Abd El ;
Abdallah, M. ;
Al-Gorair, Arej S. ;
Tirkistani, F. A. A. ;
Nooh, S. ;
Assi, R. .
INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2021, 16 (01) :1-18
12345