CorrosionbehaviorofaluminumalloysinNa2SO4solutionusingthescanningelectrochemicalmicroscopytechnique

被引：0
作者：
Herong Zhou Xiaogang Li Chaofang Dong Kui Xiao and Tai Li School of Materials Science and EngineeringUniversity of Science and Technology BeijingBeijing China Beijing Key Laboratory for CorrosionErosion and Surface TechnologyBeijing China [1 ,2 ,1 ,2 ,1 ,1 ,1 ,1 ,100083 ,2 ,100083 ]
机构：
来源：
InternationalJournalofMineralsMetallurgyandMaterials | 2009年 / 15卷 / 01期
关键词：
aluminum alloys; corrosion behavior; intermetallic particles; scanning electrochemical microscopy(SECM);
D O I：
暂无
中图分类号：
TG172 [各种类型的金属腐蚀];
学科分类号：
080503 ;
摘要：
The corrosion behavior of aluminum alloys 1060 and 2A12 in a 10 mM Na2SO4+5 mM KI solution was investigated by scanning electrochemical microscopy(SECM) and scanning electron microscopy(SEM) . The potential topography and corrosion morphology results show that the potential of the sample surface over the same area changes with the increase of immersion time. The corrosion area becomes large,and the potential becomes more negative. The corrosion potential of the 2A12 alloy surface is lower than that of 1060 aluminum,and 2A12 alloy becomes easily corrosive. This is the reason that preferential dissolution in the boundary region of some intermetallic particles(IMPs) occurs and different dissolution behaviors are associated with different types of IMPs because of different potentials.
引用
收藏
页码：84 / 88
页数：5
相关论文
共 50 条
[21]   Probing the friction and wear behaviors of diamond-like carbon film in HCl and H2SO4 media [J].
Gou, Chengxue ;
Shang, Lunlin ;
Lu, Zhibin ;
Zhang, Guangan ;
Wang, Shunhua ;
Wu, Zhiguo .
MATERIALS RESEARCH EXPRESS, 2019, 6 (10)
[22]   PASSIVATION STUDY OF Ti3AlC2 AND Ti2AlC IN SELECT ACIDIC SOLUTIONS H2SO4, HCl AND HNO3 [J].
Aouchiche, Lylia ;
Boudinar, Salem ;
Alhussein, Akram ;
Nechiche, Mustapha ;
Azem, Said .
UNIVERSITY POLITEHNICA OF BUCHAREST SCIENTIFIC BULLETIN SERIES B-CHEMISTRY AND MATERIALS SCIENCE, 2020, 82 (01) :187-198
[23]   The Corrosion Behavior of Pure Iron under Solid Na2SO4 Deposit in Wet Oxygen Flow at 500 °C [J].
Tang, Yanbing ;
Liu, Li ;
Fan, Lei ;
Li, Ying ;
Wang, Fuhui .
MATERIALS, 2014, 7 (09) :6144-6157
[24]   Effect of Welding Thermal Cycle on Corrosion Behavior of Q315NS Steel in H2SO4 Solution [J].
Zhang Suqiang ;
Zhao Hongyun ;
Shu Fengyuan ;
Wang Guodong ;
He Wenxiong .
ACTA METALLURGICA SINICA, 2017, 53 (07) :808-816
[25]   Electrochemical Behavior Assessment of Micro- and Nano-Grained Commercial Pure Titanium in H2SO4 Solutions [J].
Fattah-alhosseini, Arash ;
Ansari, Ali Reza ;
Mazaheri, Yousef ;
Karimi, Mohsen .
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2017, 26 (02) :611-620
[26]   Effect of Mg and Sn Addition on the Corrosion Behavior of an Al-Mn Alloy in 0.5 M H2SO4 [J].
Vuelvas, S. ;
Valdez, S. ;
Gonzalez-Rodriguez, J. G. .
INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2012, 7 (05) :4171-4181
[27]   The roles of Al2Cu and of dendritic refinement on surface corrosion resistance of hypoeutectic Al-Cu alloys immersed in H2SO4 [J].
Osorio, Wislei R. ;
Spinelli, Jose E. ;
Freire, Celia M. A. ;
Cardona, Margarita B. ;
Garcia, Amauri .
JOURNAL OF ALLOYS AND COMPOUNDS, 2007, 443 (1-2) :87-93
[28]   The roles of Al2Cu and of dendritic refinement on surface corrosion resistance of hypoeutectic Al-Cu alloys immersed in H2SO4 [J].
Osório, Wislei R. ;
Spinelli, José E. ;
Freire, Célia M.A. ;
Cardona, Margarita B. ;
Garcia, Amauri .
Journal of Alloys and Compounds, 2007, 443 (1-2) :87-93
[29]   Passivation Behavior of Al88Fe6La6 Glassy Alloy in NaOH and H2SO4 Solutions [J].
Li, R. ;
Li, X. Y. ;
Pang, J. ;
Yin, L. J. ;
Zhang, H. D. ;
Cao, C. D. ;
Wang, W. M. .
INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2013, 8 (02) :2983-2995
[30]   Corrosion Behavior and Biocompatibility of Hydroxyapatite Coating on H2SO4 Passivated 316L SS for Human Body Implant [J].
Parsapour, Ali ;
Khorasani, Saied Nonni ;
Fathi, Mohammad Hossein .
ACTA METALLURGICA SINICA-ENGLISH LETTERS, 2013, 26 (04) :409-415
12345