Effects of 405 stainless steel on crevice corrosion behavior of Alloy690 in high-temperature pure water

被引：9
作者：
Fangqiang Ning [1 ,2 ]
Jibo Tan [1 ]
Xinqiang Wu [1 ]
机构：
[1] CAS Key Laboratory of Nuclear Materials and Safety Assessment, Liaoning Key Laboratory for Safety and Assessment Technique of Nuclear Materials,Institute of Metal Research, Chinese Academy of Sciences
[2] School of Materials Science and Engineering, University of Science and Technology of China
来源：
Journal of Materials Science & Technology | 2020年 / 47卷 / 12期
关键词：
Alloy; High-temperature corrosion; Crevice corrosion; Oxidation;
D O I：
暂无
中图分类号：
TG172.2 [接触腐蚀、缝隙腐蚀、摩擦腐蚀];
学科分类号：
080503 ;
摘要：
Effects of 405 stainless steel（405 SS） on crevice corrosion behavior of Alloy 690 in high-temperature pure water were investigated.Results revealed that the corrosion rate of Alloy 690 was low within the crevice.It was likely attributed to the fact that a Cr-rich inner oxide film and a Ni-rich layer beneath this oxide film formed upon Alloy 690,inhibiting the diffu sion of oxygen towards the oxide/matrix interface.Moreover,the Fe2+ions dissolved from 405 SS consumed most of oxygen,leading to less oxygen participating in the oxidation of Alloy 690.In addition,it was found that Fe concentration continuously decreased from the surface of the inner oxide film to the oxide/matrix interface of Alloy 690 within the crevice,which was probably due to the diffusion of Fe2+ions dissolved from 405 SS into the inner oxide film.
引用
收藏
页码：76 / 87
页数：12
相关论文
共 50 条
[41]   The Effects of Cl- and Selected Deoxidizers on the High-Temperature Corrosion Electrochemistry of Alloy 690 in Nuclear Steam Generator Water [J].
Wang, Rui ;
Huang, Jing ;
Sun, Changshuai ;
Li, Xuejin ;
Qian, Baozhi ;
Zhao, Zhimin .
CORROSION, 2024, 80 (07) :693-704
[42]   Effects of normal load on fretting corrosion fatigue of Alloy 690 in 285 °C pure water [J].
Liao, Jiapeng ;
Tan, Jibo ;
Wu, Xinqiang ;
Tang, Lichen ;
Qian, Hao ;
Xie, Yongcheng .
CORROSION SCIENCE, 2018, 141 :158-167
[43]   Corrosion fatigue behavior of 304 stainless steel notched specimen in high temperature pressurized water [J].
Liao, Jiapeng ;
Tan, Jibo ;
Wu, Xinqiang ;
Ning, Dong ;
Xue, Guohong ;
Yao, Weida .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2019, 748 :137-145
[44]   Corrosion fatigue crack growth behavior of 316LN stainless steel in high-temperature pressurized water [J].
Zhang, Ziyu ;
Tan, Jibo ;
Wu, Xinqiang ;
Han, En-Hou ;
Ke, Wei .
NUCLEAR ENGINEERING AND TECHNOLOGY, 2021, 53 (09) :2977-2981
[45]   Study on High-temperature Corrosion Behavior of 304 Stainless Steel in Molten Sodium Polysulfide [J].
Yao Y. ;
Ren Y. ;
Peng Y. ;
Chen J. ;
Qiu W. ;
Zhou L. .
Cailiao Daobao/Materials Reports, 2023, 37 (14)
[46]   Electrochemical interaction of lead with alloy 600 and alloy 690 in high-temperature water [J].
Hwang, SS ;
Kim, JS .
CORROSION, 2002, 58 (05) :392-398
[47]   Comparative corrosion behavior of Alloys 690 and 800 in high-temperature water: Combined effects of polyacrylic acid and dissolved oxygen [J].
Zhang, Zhiyuan ;
Zhang, Zhiming ;
Wang, Jianqiu ;
Ming, Hongliang ;
Zhu, Haipeng ;
Han, En-Hou .
CORROSION SCIENCE, 2025, 245
[48]   Investigation on the failure mechanistic evolution of fretting corrosion of Alloy 690 with increasing cycles in high-temperature water [J].
Zhuang, Wenhua ;
Han, Zhongli ;
Huang, Qian ;
Qi, Huanhuan ;
Zhang, Lefu ;
Guo, Xianglong .
JOURNAL OF NUCLEAR MATERIALS, 2024, 591
[49]   Surface Oxidation and Subsurface Microstructure Evolution of Alloy 690TT Induced by Partial Slip Fretting Corrosion in High-Temperature Pure Water [J].
Long Xin ;
Yongming Han ;
Ligong Ling ;
Yonghao Lu ;
Tetsuo Shoji .
Acta Metallurgica Sinica (English Letters), 2021, 34 :543-554
[50]   Effect of grain boundary engineering on corrosion fatigue behavior of 316LN stainless steel in borated and lithiated high-temperature water [J].
Gao, Jun ;
Tan, Jibo ;
Wu, Xinqiang ;
Xia, Shuang .
CORROSION SCIENCE, 2019, 152 :190-201
12345