Effects of 405 stainless steel on crevice corrosion behavior of Alloy690 in high-temperature pure water

被引：9
作者：
Fangqiang Ning [1 ,2 ]
Jibo Tan [1 ]
Xinqiang Wu [1 ]
机构：
[1] CAS Key Laboratory of Nuclear Materials and Safety Assessment, Liaoning Key Laboratory for Safety and Assessment Technique of Nuclear Materials,Institute of Metal Research, Chinese Academy of Sciences
[2] School of Materials Science and Engineering, University of Science and Technology of China
来源：
Journal of Materials Science & Technology | 2020年 / 47卷 / 12期
关键词：
Alloy; High-temperature corrosion; Crevice corrosion; Oxidation;
D O I：
暂无
中图分类号：
TG172.2 [接触腐蚀、缝隙腐蚀、摩擦腐蚀];
学科分类号：
080503 ;
摘要：
Effects of 405 stainless steel（405 SS） on crevice corrosion behavior of Alloy 690 in high-temperature pure water were investigated.Results revealed that the corrosion rate of Alloy 690 was low within the crevice.It was likely attributed to the fact that a Cr-rich inner oxide film and a Ni-rich layer beneath this oxide film formed upon Alloy 690,inhibiting the diffu sion of oxygen towards the oxide/matrix interface.Moreover,the Fe2+ions dissolved from 405 SS consumed most of oxygen,leading to less oxygen participating in the oxidation of Alloy 690.In addition,it was found that Fe concentration continuously decreased from the surface of the inner oxide film to the oxide/matrix interface of Alloy 690 within the crevice,which was probably due to the diffusion of Fe2+ions dissolved from 405 SS into the inner oxide film.
引用
收藏
页码：76 / 87
页数：12
相关论文
共 50 条
[1]   Effects of 405 stainless steel on crevice corrosion behavior of Alloy 690 in high-temperature pure water [J].
Ning, Fangqiang ;
Tan, Jibo ;
Wu, Xinqiang .
JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2020, 47 :76-87
[2]   Crevice corrosion behavior of Alloy 690 in high-temperature water [J].
Ning, Fangqiang ;
Wu, Xinqiang ;
Tan, Jibo .
JOURNAL OF NUCLEAR MATERIALS, 2019, 515 :326-337
[3]   Effects of crevice geometry on corrosion behavior of 304 stainless steel during crevice corrosion in high temperature pure water [J].
Chen, Dongxu ;
Han, En-Hou ;
Wu, Xinqiang .
CORROSION SCIENCE, 2016, 111 :518-530
[4]   Crevice Corrosion Behavior of Alloy 690 in High-Temperature Aerated Chloride Solution [J].
Ning, Fangqiang ;
Tan, Jibo ;
Zhang, Ziyu ;
Wang, Xiang ;
Wu, Xinqiang ;
Han, En-Hou ;
Ke, Wei .
MATERIALS, 2022, 15 (15)
[5]   Oxidation Behavior of 304 Stainless Steel During Crevice Corrosion in High-Temperature Pure Water [J].
Chen, Dongxu ;
Wu, Xinqiang ;
Han, En-Hou ;
Sun, Haitao .
CORROSION, 2015, 71 (10) :1213-1223
[6]   Effects of Temperature on Fretting Corrosion Between Alloy 690TT and 405 Stainless Steel in Pure Water [J].
Liu, Xing-Chen ;
Ming, Hong-Liang ;
Zhang, Zhi-Ming ;
Wang, Jian-Qiu ;
Tang, Li-Chen ;
Qian, Hao ;
Xie, Yong-Cheng ;
Han, En-Hou .
ACTA METALLURGICA SINICA-ENGLISH LETTERS, 2019, 32 (12) :1437-1448
[7]   Effects of thiosulfate and dissolved oxygen on crevice corrosion of Alloy 690 in high-temperature chloride solution [J].
Ning, Fangqiang ;
Tan, Jibo ;
Zhang, Ziyu ;
Wu, Xinqiang ;
Wang, Xiang ;
Han, En-Hou ;
Ke, Wei .
JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2021, 66 :163-176
[8]   Fretting corrosion fatigue of Alloy 690 in high-temperature pure water [J].
Liao, Jiapeng ;
Wu, Xinqiang ;
Tan, Jibo ;
Tang, Lichen ;
Qian, Hao ;
Xie, Yongcheng .
CORROSION SCIENCE, 2018, 133 :423-431
[9]   Crevice corrosion behaviors of Alloy 690 and 405 stainless steel in chloride solutions with different concentrations of thiosulfate [J].
Ning, Fangqiang ;
Tan, Jibo ;
Zhang, Ziyu ;
Wang, Xiang ;
Wu, Xinqiang ;
Han, En-Hou ;
Ke, Wei .
JOURNAL OF NUCLEAR MATERIALS, 2023, 575
[10]   Effects of Temperature on Fretting Corrosion Between Alloy 690TT and 405 Stainless Steelin Pure Water [J].
XingChen Liu ;
HongLiang Ming ;
ZhiMing Zhang ;
JianQiu Wang ;
LiChen Tang ;
Hao Qian ;
YongCheng Xie ;
EnHou Han .
ActaMetallurgicaSinica(EnglishLetters), 2019, 32 (12) :1437-1448
12345