The microstructure of high vanadium and cobalt high speed steel(high-V/Co HSS) and the morphology of its carbides were analyzed by optical microscope(OM),scanning electron microscope(SEM),electron probe microanalysis(EPMA),X-ray power diffraction(XRD),atomic force microscopy(AFM) and single phase erosion(SPE).The results suggest that the as-sprayed high-V/Co HSS has fine equiaxed grains(about 20 μm in size),which were homogeneously distributed.The carbides have two classical morphologies:one is fine particles(about 2 μm in size) distributed along the grain boundaries and the other is needle-like one,distributed on the grain boundaries.There are MC carbides,M2C carbides,M6C carbides and Cr2WC2 carbides in the as-sprayed high-V/Co HSS samples,however,in the as-cast high-V/Co HSS,there are MC carbides and Cr2WC2 carbides only.The SPE results show that there are two types of MC carbides in the as-sprayed HSS:the sphere one and the particle-like one.The former is about 2 μm in size and the latter is less than 1 μm,dispersed inside the grains,quite different from the MC carbides in the as-cast HSS.According to the AFM results,the skeleton-like M6C carbides of the as-sprayed high-V/Co HSS are embedded in the matrix along the grain boundaries.It is found that there are sharp membrane pieces on the carbides.Some small bamboo-shoot-like MC carbides grow from the matrix and are dispersed inside the grain.Those larger MC carbides are spherical particles embedded at the grain boundary junctions.