Formation and Mechanical Properties of Zr-Nb-Cu-Ni-Al-Lu Bulk Glassy Alloys with Superior Glass-Forming Ability

被引：0

作者：

赵相金 ^{[1
]}

LIU Wei ^{[1
]}

LIU Li ^{[1
]}

ZHANG Tao ^{[2
]}

PANG Shujie ^{[2
]}

MA Chaoli ^{[2
]}

机构：

[1] School of Environment and Materials Engineering,Yantai University

[2] Department of Materials Science and Engineering,Beijing University of Aeronautics and Astronautics

来源：

JournalofWuhanUniversityofTechnology(MaterialsScience) | 2016年 / 31卷 / 01期

基金：

中国国家自然科学基金;

关键词：

metallic glass; zirconium-based alloy; glass-forming ability; mechanical properties;

D O I：

暂无

中图分类号：

TG139.8 [];

学科分类号：

080502 ;

摘要：

Glass-forming ability(GFA) and mechanical properties of(ZrNbCuNiAl)Lu(x= 0-3 at%) alloys have been investigated.The GFA of ZrNbCuNiAlalloy is dramatically enhanced by adding Lu.The(ZrNbCuNiAl)Lualloy possesses the highest GFA in the studied Zr-Nb-Cu-Ni-Al-Lu alloys,with its critical diameter for glass formation reaching 20 mm by copper-mould casting method,while that of the Lu-free ZrNbCuNiAlalloy is 7 mm.The critical diameters of(ZrNbCuNiAl)Lu(x =1 at%and 3 at%) alloys are 15 mm and 12 mm,respectively.The Lu addition to ZrNbCuNiAlalloy induces the change of initial crystallization phases from face-centred-cubic ZrNi and tetragonal ZrNi phases for the Lu-free ZrNbCuNiAlalloy to an icosahedral quasi-crystalline phase for the Lu-doped alloys,which may be the origin for the enhanced GFA of the Lu-doped alloys.The compressive fracture strength and plastic strain of the bulk glassy(ZrNbCuNiAl)Lualloy are1 610 MPa and 1.5%,respectively.

引用

页码：186 / 190

页数：5

共 50 条

[21] Effects of Cr addition on glass-forming ability and mechanical properties of Cu–Zr–Al bulk metallic glass
W. Zhou
L. T. Kong
J. F. Li
Y. H. Zhou
Journal of Materials Science, 2012, 47 : 4996 - 5001
[22] Crystallization, mechanical and corrosion properties of Zr-Cu-Ni-Al-Nb bulk glassy alloys
Lin, L
Sun, M
Chen, Q
Liu, B
Qiu, CL
ACTA PHYSICA SINICA, 2006, 55 (04) : 1930 - 1935
[23] Glass-forming ability and mechanical properties of Cu50Zr50-xTix alloys
Men, H
Pang, SJ
Zhang, T
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2005, 408 (1-2): : 326 - 329
[24] Effect of Fe on the glass-forming ability, structure and devitrification behavior of Zr-Cu-Al bulk glass-forming alloys
Louzguine-Luzgin, Dmitri V.
Xie, Guoqiang
Zhang, Qingsheng
Inoue, Akihisa
PHILOSOPHICAL MAGAZINE, 2010, 90 (14) : 1955 - 1968
[25] Ni-free Zr-Fe-Al-Cu bulk metallic glasses with high glass-forming ability
Zhang, Q. S.
Zhang, W.
Inoue, A.
SCRIPTA MATERIALIA, 2009, 61 (03) : 241 - 244
[26] Glass forming ability & mechanical properties of Fe-Ni-Zr-Si-B bulk glassy alloys
Lee, KA
Namkung, J
Kim, MC
PRICM 5: THE FIFTH PACIFIC RIM INTERNATIONAL CONFERENCE ON ADVANCED MATERIALS AND PROCESSING, PTS 1-5, 2005, 475-479 : 3405 - 3408
[27] Zr-Cu-Ni-Al bulk metallic glasses with superhigh glass-forming ability
Sun, Y. J.
Qu, D. D.
Huang, Y. J.
Liss, K. -D.
Wei, X. S.
Xing, D. W.
Shen, J.
ACTA MATERIALIA, 2009, 57 (04) : 1290 - 1299
[28] The effect of Ta addition on the glass forming ability and mechanical properties of Ni-Zr-Nb-Al metallic glass alloys
Na, J. H.
Park, J. M.
Han, K. H.
Park, B. J.
Kim, W. T.
Kim, D. H.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 431 (1-2): : 306 - 310
[29] Structure and mechanical properties of bulk glass-forming Ni-Nb-Sn alloys
Choi-Yim, H
Xu, DH
Lind, ML
Löffler, JF
Johnson, WL
SCRIPTA MATERIALIA, 2006, 54 (02) : 187 - 190
[30] Formation and mechanical properties of Zr-Cu-Al bulk glassy alloys
Yokoyama, Y
Fukaura, K
Inoue, A
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 375 : 427 - 431

← 1 2 3 4 5 →