Three new catalysts based on the silica gel supported polyether ionic liquids（ILs）, i.e., [HO-PECH-MIM]ClSi, [H2N-PECH-MIM]Cl-Si, and [HOOC-PECH-MIM]Cl-Si, were prepared, and their chemical structures were characterized by infrared（IR） spectroscopy and nuclear magnetic resonance（NMR） spectroscopy. Thermogravimetric analyzer（TG）, X-ray diffractometer（XRD） and scanning electron microscope（SEM） were used to evaluate their thermal stability,crystalline structure and apparent morphology, respectively. Surface areas of the prepared catalysts were calculated by the Brunauer-Emmett-Teller（BET） method. The catalytic reaction for the synthesis of propylene carbonate（PC） using CO;and propylene oxide（PO） in the presence of the prepared catalysts was studied. The influences of times of recycling and catalyst structure on catalytic performance were also investigated. The experimental results showed that the silica gel supported polyether ILs catalysts successfully prepared under mild condition could possess the advantages of high activity, excellent thermal stability, good selectivity and easy recycling, while the phase transition of the liquid polyether ILs catalysts was also achieved. When the reaction temperature was 90 °C, the CO;pressure was 2.0 MPa and the dosage of the catalyst was 2.5%, [HOOC-PECH-MIM]Cl-Si was found to have the best catalytic performance in the catalytic process, with the conversion rate reaching 100% and the selectivity equating to 98.2%. The conversion rate and selectivity still could reach more than 90% even after the catalyst was reused for 15 times.