DUCTILEBRITTLETRANSITION OF POLYCRYSTALLINE Ni3Al WITH VARYING GRAIN SIZE

It is known that in B (un)doped Ni 3Al polycrystals, the dependence of yield strength on grain size follows the Hall Petch relationship: σ y= σ 0+ K y d -1/2 , and the slope K y can be reduced by B doping owing to the lowering of grain boundary resistance to slip transmission. If the intergranular cracking in polycrystalline Ni 3Al occurs from the microcavity along the grain boundaries, the effective external tensile stress for the propagation of the crack like microcavity along the grain boundaries can be deduced as: σ f= σ i+ K u d -1/2 , where K u reflects the effects of such factors as environment, strain rate, boron doping and the orientation of the grain boundary on the trend of intergranular cracking. For loaded polycrystalline Ni 3Al, it should be competitive between the intergranular cracking and slip transmission across the grain boundary. Therefore, comparing the varieties of both σ y and σ f with grain size, the dependence of ductile brittle transition on grain size, and the effects of the above factors on ductile brittle transition can be expected. The model also predicts that there exists a critical grain size for the ductile brittle transition of polycrystalline Ni 3Al alloys, and B doping can increase the critical grain size due to the reduction of the slope K y and the increase of K u. The reported experimental results verified the above model.