Microstructures and mechanical properties of extruded Mg-1Mn-3.5Y and Mg-1Mn-1Y-2.5Nd alloys

被引：0

作者：

房大庆 ^{[1
]}

江中浩 ^{[1
]}

毕广利 ^{[1
]}

李荣广 ^{[2
]}

李光玉 ^{[1
]}

机构：

[1] Key Laboratory of Automobile Materials,Department of Materials Science and Engineering,Jilin University

[2] College of Materials Science and Engineering,Chongqing University

来源：

Transactions of Nonferrous Metals Society of China | 2010年 / 20(S2)卷 / S2期

基金：

中国国家自然科学基金;

关键词：

magnesium alloys; earth elements; microstructures; deformation behavior; mechanical properties;

D O I：

暂无

中图分类号：

TG379 [有色金属及合金挤压];

学科分类号：

080201 ; 080503 ;

摘要：

Both Mg-1Mn-3.5Y and Mg-1Mn-1Y-2.5Nd alloys(mass fraction,%)were extruded at 380℃.Most of the(10 10) crystal planes in the Mg-1Mn-3.5Y alloy are parallel to the normal direction,while most of the(10 11)crystal planes in the Mg-1Mn-1Y-2.5Nd alloy are parallel to the normal direction.The tensile tests at room temperature,100℃ and 200℃ show that the Mg-1Mn-3.5Y alloy exhibits higher yield strength,but lower elongation to failure as compared with the Mg-1Mn-1Y-2.5Nd alloy. These differences in the tensile mechanical properties between the two alloys are mainly attributed to their different texture types and amount and distribution of the Mg24Y5 precipitates.The serration flow behavior is observed in the Mg-1Mn-1Y-2.5Nd alloy at 200℃,but does not occur in the Mg-1Mn-3.5Y alloy.The Mg-1Mn-3.5Y alloy shows the cleavage fracture mode,while the Mg-1Mn-1Y-2.5Nd alloy exhibits the dimple fracture mode.

引用

页码：555 / 560

页数：6

共 6 条

[1]

Microstructures and mechanical properties of Mg–8Gd–0.6Zr– x Nd （ x = 0, 1, 2 and 3 mass%） alloys[J] . Qiuming Peng,Yaoming Wu,Daqing Fang,Jian Meng,Limin Wang.Journal of Materials Science . 2007 (11)

[2]

Precipitation reactions in Magnesium-rare earth alloys containing Yttrium, Gadolinium or Dysprosium[J] . P.J. Apps,H. Karimzadeh,J.F. King,G.W. Lorimer.Scripta Materialia . 2003 (8)

[3]

Atom probe characterization of plate-like precipitates in a Mg–RE–Zn–Zr casting alloy[J] . D.-H. Ping,K. Hono,J.F. Nie.Scripta Materialia . 2003 (8)

[4]

Hardening precipitation in a Mg–4Y–3RE alloy[J] . C. Antion,P. Donnadieu,F. Perrard,A. Deschamps,C. Tassin,A. Pisch.Acta Materialia . 2003 (18)

[5] The activity of non-basal slip systems and dynamic recovery at room temperature in fine-grained AZ31B magnesium alloys [J].

Koike, J ;

Kobayashi, T ;

Mukai, T ;

Watanabe, H ;

Suzuki, M ;

Maruyama, K ;

Higashi, K .

ACTA MATERIALIA, 2003, 51 (07) :2055-2065

[6]

Development of Mg–Sc–Mn alloys[J] . F. von Buch,J. Lietzau,B.L. Mordike,A. Pisch,R. Schmid-Fetzer.Materials Science ＆ Engineering A . 1999 (1)

← 1 →