Preparation process and characterization of new Pt/stainless steel wire mesh catalyst designed for volatile organic compounds elimination

被引：0

作者：

张婷 ^{[1
]}

陈敏 ^{[1
]}

高园园 ^{[1
]}

郑小明 ^{[1
]}

机构：

[1] Institute of Catalysis, Zhejiang University

来源：

Journal of Central South University | 2012年 / 19卷 / 02期

关键词：

volatile organic compounds; anodic oxidation; electrolyte; Pd;

D O I：

暂无

中图分类号：

X701 [废气的处理与利用];

学科分类号：

083002 ;

摘要：

A novel 0.1% Pd-0.05% (mass fraction) Pt/stainless steel wire mesh catalyst was prepared for volatile organic compounds (VOCs) elimination. The catalyst was synthesized by stainless steel wire mesh as support and then treated by anodic oxidation technology to develop a porous membrane on the support. During the anodic oxidation process, various electrolytes were used to investigate the formation of porous membrane. And the catalytic performance of the catalysts was tested by using toluene and acetone combustion as model reaction. The temperatures of complete toluene and acetone conversion were decreased to 180 °C and 240 °C, respectively. The morphologies of the stainless steel wire mesh supports and catalysts were characterized by means of scanning electron microscopy (SEM) and temperature-programmed reduction (TPR).

引用

页码：319 / 323

页数：5

共 10 条

[1] Effect of anodic alumina pore diameter variation on template-initiated synthesis of carbon nanotube catalyst supports[J] . S. Sigurdson,V. Sundaramurthy,A.K. Dalai,J. Adjaye. Journal of Molecular Catalysis. A, Chemical . 2009 (1)
[2] Development of the HYD route of hydrodesulfurization of dibenzothiophenes over Pd–Pt/ γ -Al 2 O 3 catalysts[J] . V.G. Baldovino-Medrano,P. Eloy,E.M. Gaigneaux,Sonia A. Giraldo,Aristóbulo Centeno. Journal of Catalysis . 2009 (2)
[3] Hydrodesulfurization of 4,6-dimethyldibenzothiophene and dibenzothiophene over alumina-supported Pt, Pd, and Pt-Pd catalysts[J] . Journal of Catalysis . 2006 (1)
[4] Evaluation of wire-mesh honeycomb containing porous Al/Al 2 O 3 layer for catalytic combustion of ethyl acetate in air[J] . Kyung Shik Yang,Jin Seong Choi,Jong Shik Chung. Catalysis Today . 2004 (2)
[5] Synthesis and characterization of MCM-41 coatings on stainless steel grids
Louis, B
Subrahmanyam, C
Kiwi-Minsker, L
Viswanathan, B
Buffat, PA
Renken, A
[J]. CATALYSIS COMMUNICATIONS, 2002, 3 (04) : 159 - 163
[6] Synthesis of high-ordered LiCoO 2 nanowire arrays by AAO template[J] . Yingke Zhou,Chengmin Shen,Hulin Li. Solid State Ionics . 2002 (1)
[7] Thermal anisotropy in sintered cordierite monoliths[J] . B.P Saha,Roy Johnson,I Ganesh,G.V.N Rao,S Bhattacharjee,Y.R Mahajan. Materials Chemistry and Physics . 2001 (1)
[8] Optimization of the preparation of binderless ZSM-5 coatings on stainless steel monoliths by in situ hydrothermal synthesis
Shan, Z
van Kooten, WEJ
Oudshoorn, OL
Jansen, JC
van Bekkum, H
van den Bleek, CM
Calis, HPA
[J]. MICROPOROUS AND MESOPOROUS MATERIALS, 2000, 34 (01) : 81 - 91
[9] A remarkable synergic effect of water-soluble bimetallic catalyst in the hydrogenation of aromatic nitrocompounds
Jiang, H
Xu, Y
Liao, SJ
Yu, DR
Chen, H
Li, XJ
[J]. JOURNAL OF MOLECULAR CATALYSIS A-CHEMICAL, 1999, 142 (02) : 147 - 152
[10] Development of catalytic combustion technology of VOC materials by anodic oxidation catalyst[J] . Intan E. Sungkono,Hideo Kameyama,Toshiyuki Koya. Applied Surface Science . 1997

← 1 →