ElectrochemicalperformanceofLiFePO4/(C+Fe2P)compositecathodematerialsynthesizedbysol-gelmethod

被引:0
作者
陈权启 [1 ,2 ]
李小栓 [1 ]
王建明 [2 ]
机构
[1] Key Laboratory of Environmentally Friendly Chemistry and Applications of Ministry of Education,School of Chemistry,Xiangtan University
[2] Department of Chemistry,Zhejiang University
关键词
LiFePO4/(C+Fe2P) composite; sol-gel; sphere-like morphology; electrochemical performance;
D O I
暂无
中图分类号
TB332 [非金属复合材料];
学科分类号
0805 ; 080502 ;
摘要
A LiFePO4/(C+Fe2P) composite cathode material was prepared by a sol-gel method using Fe(NO3)3·9H2O,LiAc·H2O,NH4H2PO4 and citric acid as raw materials,and the physical properties and electrochemical performance of the composite cathode material were investigated by X-ray diffractometry(XRD),scanning electron microscopy(SEM),transmission electron microscopy(TEM) and electrochemical tests.The Fe2P content,morphology and electrochemical performance of LiFePO4/(C+Fe2P) composite depend on the calcination temperature.The optimized LiFePO4/(C+Fe2P) composite is prepared at 650 °C and the optimized composite exhibits sphere-like morphology with porous structure and Fe2P content of about 3.2%(mass fraction).The discharge capacity of the optimized LiFePO4/(C+Fe2P) at 0.1C is 156 and 161 mA·h/g at 25 and 55 °C,respectively,and the corresponding capacity retentions are 96% after 30 cycles;while the capacity at 1C is 142 and 149 mA·h/g at 25 and 55 °C,respectively,and the capacity still remains 135 and 142 mA·h/g after 30 cycles at 25 and 55 °C,respectively.
引用
收藏
页码:978 / 984
页数:7
相关论文
共 50 条
[41]   In situ modification of LiMn3/4Fe1/4PO4/C cathode realized by hierarchical porous ?-LiAlO2 as channel for lithium-ion batteries [J].
Chang, Longjiao ;
Bi, Xiaolong ;
Yang, Wei ;
Wei, Anlu ;
Yang, Ruifen ;
Liu, Jianan .
JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 2023, 936
[42]   Li2FeSiO4/C cathode material synthesized by template-assisted sol-gel process with Fe2O3 microsphere [J].
Qu, Long ;
Fang, Shaohua ;
Yang, Li ;
Hirano, Shin-ichi .
JOURNAL OF POWER SOURCES, 2012, 217 :243-247
[43]   MoS2 Decorated Fe3O4/Fe1-xS@C Nanosheets as High-Performance Anode Materials for Lithium Ion and Sodium Ion Batteries [J].
Pan, Qichang ;
Zheng, Fenghua ;
Ou, Xing ;
Yang, Chenghao ;
Xiong, Xunhui ;
Tang, Zhenghua ;
Zhao, Lingzhi ;
Liu, Meilin .
ACS SUSTAINABLE CHEMISTRY & ENGINEERING, 2017, 5 (06) :4739-4745
[44]   Effects of surfactant-assisted synthesis Fe3(PO4)2•8H2O and its purity and morphology on the performance of LiFePO4/C cathode materials [J].
Zheng, Yi ;
Tian, Weichao ;
Cao, Jingrui ;
Zhang, Kaicheng ;
Tian, Shiyu ;
Wang, Li ;
Liang, Guangchuan .
IONICS, 2020, 26 (11) :5445-5453
[45]   A high performance fiber-shaped PEDOT@MnO2//C@Fe3O4 asymmetric supercapacitor for wearable electronics [J].
Sun, Jinfeng ;
Huang, Yan ;
Fu, Chenxi ;
Huang, Yang ;
Zhu, Minshen ;
Tao, Xiaoming ;
Zhi, Chunyi ;
Hu, Hong .
JOURNAL OF MATERIALS CHEMISTRY A, 2016, 4 (38) :14877-14883
[46]   Microwave-Solvothermal Synthesis of Nanostructured Li2MSiO4/C (M = Mn and Fe) Cathodes for Lithium-Ion Batteries [J].
Muraliganth, T. ;
Stroukoff, K. R. ;
Manthiram, A. .
CHEMISTRY OF MATERIALS, 2010, 22 (20) :5754-5761
[47]   A novel synthesis of LiFePO4/C from Fe2O3 without extra carbon or carbon-containing reductant [J].
Xiao Zheng-wei ;
Hu Guo-rong .
JOURNAL OF CENTRAL SOUTH UNIVERSITY, 2014, 21 (06) :2143-2149
[48]   Synthesis of Mg-LiFePO4/C composite using intermediate FePO4•2H2O from Fe3(PO4)2•8H2O as precursor via an aqueous rheological phase assisted method [J].
Li, Yuanchao ;
Hao, Jinghao ;
Wei, Fengli ;
Fu, Lei ;
Liu, Yu ;
Wang, Zhongju ;
Yang, Changchun ;
Li, Baojun .
JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, 2016, 27 (09) :9398-9404
[49]   Synthesis of Mg-LiFePO4/C composite using intermediate FePO4·2H2O from Fe3(PO4)2·8H2O as precursor via an aqueous rheological phase assisted method [J].
Yuanchao Li ;
Jinghao Hao ;
Fengli Wei ;
Lei Fu ;
Yu Liu ;
Zhongju Wang ;
Changchun Yang ;
Baojun Li .
Journal of Materials Science: Materials in Electronics, 2016, 27 :9398-9404
[50]   ZnCo2O4 nanoflakes loaded on a Cu-supported Fe2O3-C network as an integrated lithium-ion battery anode [J].
Wang, Liting ;
Yang, Qi .
JOURNAL OF ALLOYS AND COMPOUNDS, 2019, 792 :750-758