High-speed imaging observation on molten bridges of AgNi10 electrical contact material

被引：0

作者：

Jing-Hong Chen ^{[1
]}

Song Chen ^{[1
]}

Ming Xie ^{[1
]}

Jie-Qiong Hu ^{[1
]}

Sai-Bei Wang ^{[1
]}

机构：

[1] State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metal,Kunming Institute of Precious Metals

来源：

Rare Metals | 2023年 / 42卷 / 01期

基金：

中国国家自然科学基金;

关键词：

D O I：

暂无

中图分类号：

TG146.32 [];

学科分类号：

080502 ;

摘要：

The electrical contact-high-speed imaging experimental system was developed to investigate the molten bridge phenomena of AgNi10 electrical contact material.The dimension of molten bridges was measured along with the measurement of waveforms in the contact voltage under the load of direct current(DC) 6 V(8-20 A)and breaking speed of 50.0 mm·s-1.A part of the observed results was presented as well as surface morphology of the contacts after electrical contact behavior,which shows some interesting and new phenomena.Molten bridges and arc could exist simultaneously.The stable molten bridge looks like cylindrical shape and then becomes needle tip at its rupture,the diameter and length of molten bridges both increase with the increase in current and the growth gradient of the diameter is larger than that of the length.The morphology and elemental distribution of the contact surface are changed by the behavior of electrical contact.

引用

页码：336 / 345

页数：10

共 22 条

[1] Formation Process of Intermittent Molten Bridge Between Au-Plated Contacts at Super Low Breaking Velocity[J]. 任万滨,常成,陈宇.Plasma Science and Technology. 2016(03)
[2] Preparation and microstructure characterization of a nano-sized Ti4+-doped AgSnO2 electrical contact material[J]. ZHENG Ji, LI Songlin, DOU Fuqi, and LI Tonghui Tianjin Key Laboratory of Composite and Functional Materials, School of Materials Science and Engineering, Tianjin University, Tianjin 300072, China.Rare Metals. 2009(01)
[3] Investigation of the Surface Adhesion Phenomena and Mechanism of Gold-Plated Contacts at Superlow Making/Breaking Speed
Ren, Wanbin
Chang, Cheng
Chen, Yu
Xue, Shengjun
Coutu, Ronald A., Jr.
[J]. IEEE TRANSACTIONS ON COMPONENTS PACKAGING AND MANUFACTURING TECHNOLOGY, 2015, 5 (06): : 771 - 778
[4] Experimental Analysis of Arc Waveform Affected by Holder Temperature Change at Slowly Separation of Silver-Tin Dioxide Contacts
Kayano, Yoshiki
Miyanaga, Kazuaki
Inoue, Hiroshi
[J]. IEICE TRANSACTIONS ON ELECTRONICS, 2013, E96C (09) : 1110 - 1118
[5] Nonlinear and Negative Resistance in Loose Electrical Contacts Dark Bridge[J] . Hiromichi Kubota,Shunsuke Sasaki,Hiroyuki Ishida,Tasuku Takagi.American Journal of Physics and Applications . 2013 (1)
[6] Mechanical, Electrical, and Thermal Coupled-Field Simulation of a Molten Metal Bridge During Contact Separation[J] . Tan, Z.,Guan, W.,Guo, J.,Chen, S..IEEE Transactions on Components, Packaging and Manufacturing Technology . 2013 (6)
[7] Microstructures and properties of silver-based contact material fabricated by hot extrusion of internal oxidized Ag–Sn–Sb alloy powders[J] . Canhui Xu,Danqing Yi,Chunping Wu,Huiqun Liu,Weizhou Li.Materials Science ＆ Engineering A . 2012
[8] Random Occurrence of Contact Welding in Electrical Endurance Tests
Zhao, Laijun
Li, Zhenbiao
Zhang, Hansi
Hasegawa, Makoto
[J]. IEICE TRANSACTIONS ON ELECTRONICS, 2011, E94C (09): : 1362 - 1368
[9] Effect of Heat Conductivity on Bridge Break at Different Material Contact Pairs
Miyanaga, Kazuaki
Kayano, Yoshiki
Komakine, Takashi
Inoue, Hiroshi
Takagi, Tasuku
[J]. IEICE TRANSACTIONS ON ELECTRONICS, 2011, E94C (09) : 1431 - 1434
[10] Computerized measurement stands for testing static and dynamic electrical contact welding
Borkowski, P.
Walczuk, E.
[J]. MEASUREMENT, 2011, 44 (09) : 1618 - 1627

← 1 2 3 →