Stress Analysis of CaO-Al2O3-SiO2 System Glass-ceramic with Different Thickness

被引：0
|
作者：
程金树
谢俊
机构：
[1] Wuhan University of Technology Wuhan 430070 China
[2] Key Lab of Silicate Materials Science and Engineering Ministry of Education
[3] Key Lab of Silicate Materials Science and Engineering Ministry of Education
来源：
JournalofWuhanUniversityofTechnology-MaterialsScience | 2005年 / 04期
关键词：
glass-ceramics; residual stress; CaO-Al2O3-SiO2; system;
D O I：
暂无
中图分类号：
TQ171.7 [各种玻璃产品];
学科分类号：
0805 ; 080502 ;
摘要：
In order to study the relationship between thickness and residual stress in CaO-Al2O3-SiO2 glass-ceramics.The residual stress was measured in CaO-Al2O3-SiO2 system glass-ceramic with different thickness,and the formation mechanism and characterization of residual stress in CAS system Glass-ceramic were analyzed by the X-ray diffraction analysis. The experimental results show the compressive residual stress increases with thickness of glass-ceramic increasing
引用
收藏
页码：126 / 127
页数：2
相关论文
共 50 条
  • [41] On formation of CaO-Al2O3-SiO2 glass-ceramics by vitrification of incinerator fly ash
    Cheng, TW
    Chen, YS
    CHEMOSPHERE, 2003, 51 (09) : 817 - 824
  • [42] Preparation and characterization of CaO-Al2O3-SiO2 glass-ceramics from molybdenum tailings
    Shi, Jiang
    He, Feng
    Ye, Chuqiao
    Hu, Lan
    Xie, Junlin
    Yang, Hu
    Liu, Xiaoqing
    MATERIALS CHEMISTRY AND PHYSICS, 2017, 197 : 57 - 64
  • [43] MgO-Al2O3-SiO2 Glass-Ceramic Prepared by Sol-Gel Method
    Yuan, Qiuhua
    Zhang, Peixin
    Gao, Li
    Peng, Hailin
    Ren, Xiangzhong
    Zhang, Dongyun
    POWDER TECHNOLOGY AND APPLICATION II, 2010, 92 : 131 - +
  • [44] Wollastonite-containing glass-ceramics from the CaO-Al2O3-SiO2 and CaO-MgO-SiO2 ternary systems
    Tulyaganov, Dilshat U.
    Dimitriadis, Konstantinos
    Agathopoulos, Simeon
    Baino, Francesco
    Fernandes, Hugo R.
    OPEN CERAMICS, 2024, 17
  • [45] Effect of FeO on Sintering and Leaching of Calcium Aluminates in the CaO-Al2O3-SiO2 System
    Pan, Xiaolin
    Yu, Haiyan
    Dong, Kaiwei
    Wang, Bo
    Zhang, Wu
    Bi, Shiwen
    FRONTIERS OF MATERIALS, CHEMICAL AND METALLURGICAL TECHNOLOGIES, PTS 1 AND 2, 2012, 581-582 : 1014 - 1017
  • [46] Design of a BaO-Al2O3-SiO2-B2O3 glass-ceramic for microwave LTCC substrate material based on glass-ceramic plus ceramic composite
    Mao, Haijun
    Wang, Fenglin
    Zhu, Xuelian
    Chen, Xingyu
    Li, Wei
    Zhang, Weijun
    JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, 2022, 33 (32) : 24834 - 24844
  • [47] Calculation Model of Mass Action Concentrations for CaO-Al2O3-SiO2 Slag System
    Wang, Hong-ming
    Li, Gui-rong
    Zhu, Xiang
    Zhao, Yutao
    ADVANCED MATERIALS AND PROCESS TECHNOLOGY, PTS 1-3, 2012, 217-219 : 39 - 42
  • [48] The crystallization behaviour and bioactivity of wollastonite glass-ceramic based on Na2O-K2O-CaO-SiO2-F glass system
    Salman, S. M.
    Salama, S. N.
    Abo-Mosallam, H. A.
    JOURNAL OF ASIAN CERAMIC SOCIETIES, 2015, 3 (03): : 255 - 261
  • [49] Nucleation and growth of hexagonal CaAl2Si2O8 crystals in CaO-Al2O3-SiO2 glass
    Maeda, Kei
    Yasumori, Atsuo
    MATERIALS LETTERS, 2017, 206 : 241 - 244
  • [50] Crystallization Characteristics of SiO2-Al2O3-MgO-F-ZrO2 Glass-Ceramic
    Wang Yue
    Xu Lina
    Yang Li
    Tian Qingbo
    Wang Xiuhui
    Gao Hong
    RARE METAL MATERIALS AND ENGINEERING, 2009, 38 : 1120 - 1123
12345