Stress Analysis of CaO-Al2O3-SiO2 System Glass-ceramic with Different Thickness

被引：0
|
作者：
程金树
谢俊
机构：
[1] Wuhan University of Technology Wuhan 430070 China
[2] Key Lab of Silicate Materials Science and Engineering Ministry of Education
[3] Key Lab of Silicate Materials Science and Engineering Ministry of Education
来源：
JournalofWuhanUniversityofTechnology-MaterialsScience | 2005年 / 04期
关键词：
glass-ceramics; residual stress; CaO-Al2O3-SiO2; system;
D O I：
暂无
中图分类号：
TQ171.7 [各种玻璃产品];
学科分类号：
0805 ; 080502 ;
摘要：
In order to study the relationship between thickness and residual stress in CaO-Al2O3-SiO2 glass-ceramics.The residual stress was measured in CaO-Al2O3-SiO2 system glass-ceramic with different thickness,and the formation mechanism and characterization of residual stress in CAS system Glass-ceramic were analyzed by the X-ray diffraction analysis. The experimental results show the compressive residual stress increases with thickness of glass-ceramic increasing
引用
收藏
页码：126 / 127
页数：2
相关论文
共 50 条
  • [1] Stress analysis of CaO-Al2O3-SiO2 system glass-ceramic with different thickness
    Cheng, JS
    Xie, J
    He, F
    Yang, SZ
    JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2005, 20 (04): : 126 - 127
  • [2] Stress analysis of CaO-Al2O3-SiO2 system glass-ceramic with different thickness
    Cheng J.
    Xie J.
    He F.
    Yang S.
    Journal of Wuhan University of Technology-Mater. Sci. Ed., 2005, 20 (4): : 126 - 127
  • [3] Effect of the cool system on internal stress of CaO-Al2O3-SiO2 glass-ceramic system
    Feng He
    Yong Du
    Junlin Xie
    Wenju Wang
    Journal of Wuhan University of Technology-Mater. Sci. Ed., 2007, 22 : 760 - 763
  • [4] Effect of the Cool System on Internal Stress of CaO-Al2O3-SiO2 Glass-ceramic System
    何峰
    Journal of Wuhan University of Technology(Materials Science), 2007, (04) : 760 - 763
  • [5] Effect of the cool system on internal stress of CaO-Al2O3-SiO2 glass-ceramic system
    He Feng
    Du Yong
    Xie Junlin
    Wang Wenju
    JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2007, 22 (04): : 760 - 763
  • [6] Structure Characterization of Sintered CaO-Al2O3-SiO2 Glass-ceramic Reinforced with Spodumene
    Xiao, Zi-fan
    Cheng, Jin-shu
    Xie, Jun
    RESEARCH IN MATERIALS AND MANUFACTURING TECHNOLOGIES, PTS 1-3, 2014, 835-836 : 309 - 314
  • [7] Study on application of fly-ash in CaO-Al2O3-SiO2 glass-ceramic
    He, F
    Li, QT
    Cheng, JS
    ENERGY AND ENVIRONMENT, VOLS 1 AND 2, 2003, : 1732 - 1735
  • [8] Practical strength of damage-resistant CaO-Al2O3-SiO2 glass-ceramic
    Maeda, Kei
    Akatsuka, Kosho
    Yasumori, Atsuo
    CERAMICS INTERNATIONAL, 2021, 47 (06) : 8728 - 8731
  • [9] Structure of crystalline CaAl2Si2O8 precipitated in a CaO-Al2O3-SiO2 glass-ceramic
    Akatsuka, Kosho
    Yasumori, Atsuo
    Maeda, Kei
    MATERIALS LETTERS, 2019, 242 : 163 - 165
  • [10] Effect of fluorine content on sintering and crystallisation behaviour of CaO-Al2O3-SiO2 glass ceramic system
    Banijamali, S.
    Yekta, B. Eftekhari
    Rezaie, H.
    Marghussian, V. K.
    ADVANCES IN APPLIED CERAMICS, 2008, 107 (02) : 101 - 105
12345