Effect of solidification parameters on the microstructures of a single crystal Ni-based superalloy AM3

被引:0
作者
Yu Zhuhuan Liu Lin Zhao Xinbao Zhang Weiguo Zhang Jun and Fu Hengzhi State Key Laboratory of Solidifi cation Processing Northwestern Polytechnic University Xian ChinaMaterials Science and Engineering Department Xian University of Science and Technology Xian China [1 ,2 ,1 ,1 ,1 ,1 ,1 ,1 ,710072 ,2 ,710054 ]
不详
机构
关键词
Ni-based superalloy; single crystal; withdraw rate; solidi fi cation; PDAS; SDAS;
D O I
暂无
中图分类号
TG132.32 [];
学科分类号
080502 ;
摘要
A single crystal Ni-based superalloy AM3 was processed at withdraw rates of 3.5, 10, 50, 100, 200, and 500 μm·s-1, respectively.The as-cast microstructures and solidification segregation ratio were characterized with various withdraw rates.The shape and size of carbide microstructures were determined.As expected, the primary and secondary dendrite arm spacings (PDAS and SDAS) decrease with the increase of withdraw rate.The highest volume fraction of eutectic γ/γ' is observed at the 100 μm·s-1 withdraw rate.The volume fraction of eutectic γ/γ' does not appear to be a strong function of the withdraw rate.With increasing withdraw rate, interface morphologies change in the sequence of planar, cellular, and dendrite.There is a general refinement of the microstructure as the withdraw rate increases.EPMA analysis showed that withdraw rate does not have obvious influence on the segregation of elements.
引用
收藏
页码:217 / 223
页数:7
相关论文
共 8 条
[1]  
Grain structure development in directional solidification of nickel-base superalloys[J] . A. Wagner,B.A. Shollock,M. McLean.Materials Science & Engineering A . 2004 (1)
[2]  
Directional solidification of large superalloy castings with radiation and liquid-metal cooling: A comparative assessment[J] . A. J. Elliott,T. M. Pollock,S. Tin,W. T. King,S.-C. Huang,M. F. X. Gigliotti.Metallurgical and Materials Transactions A . 2004 (10)
[3]   Influence of directional solidification variables on the cellular and primary dendrite arm spacings of PWA1484 [J].
Li, L ;
Overfelt, RA .
JOURNAL OF MATERIALS SCIENCE, 2002, 37 (16) :3521-3532
[4]   Directional solidification of Ni base superalloy IN738LC to improve creep properties [J].
Kermanpur, A ;
Varahraam, N ;
Engilehei, E ;
Mohammadzadeh, M ;
Davami, P .
MATERIALS SCIENCE AND TECHNOLOGY, 2000, 16 (05) :579-586
[5]   EFFECTS OF GROWTH-RATE ON CARBIDES AND MICROPOROSITY IN DS200+HF SUPERALLOY [J].
BALDAN, A .
JOURNAL OF MATERIALS SCIENCE, 1991, 26 (14) :3879-3890
[6]   A STATISTICALLY SIGNIFICANT EXPERIMENTAL-TECHNIQUE FOR INVESTIGATING MICROSEGREGATION IN CAST ALLOYS [J].
GUNGOR, MN .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1989, 20 (11) :2529-2533
[7]  
Effect of solidification parameters on the growth geometry of MC carbide in IN- 100 dendritic monocrystals[J] . R. Fernandez,J. C. LeComte,T. Z. Kattamis.Metallurgical Transactions A . 1978 (10)
[8]  
A New type of microstructural instability in superalloys-SRZ. W.S.Walston,J.C.Schaeffer,W.H.Murphy. Superalloys 1996 . 1996