Hot Deformation Behavior and Processing Map of Spray Formed M3∶ 2 High Speed Steel

被引:0
作者
Lin LU [1 ]
Longgang HOU [1 ]
Hua CUI [1 ]
Jinfeng HUANG [1 ]
Yongan ZHANG [2 ]
Jishan ZHANG [1 ]
机构
[1] State Key Laboratory for Advanced Metals and Materials,University of Science and Technology Beijing
[2] State Key Laboratory of Non-ferrous Metals and Process,General Research Institute for Non-ferrous Metals
关键词
high speed steel; spray forming; hot deformation; processing map; niobium;
D O I
暂无
中图分类号
TG142.45 [工具钢];
学科分类号
080502 ;
摘要
Hot deformation behavior of a new type of M3∶ 2 high speed steel with niobium addition made by spray forming was investigated based on compression tests in the temperature range of 950-1 150 ℃ and strain rate of 0. 001-10 s-1. A comprehensive constitutive equation was obtained,which could be used to predict the flow stress at different strains. Processing map was developed on the basis of the flow stress data using the principles of dynamic material model. The results showed that the flow curves were in fair agreement with the dynamic recrystallization model. The flow stresses,which were calculated by the comprehensive constitutive equation,agreed well with the test data at low strain rates( ≤1 s-1). The material constant( α),stress exponent( n) and the hot deformation activation energy( QHW) of the new steel were 0. 006 15 MPa-1,4. 81 and 546 kJ·mol-1,respectively. Analysis of the processing map with an observation of microstructures revealed that hot working processes of the steel could be carried out safely in the domain( T = 1 050-1 150 ℃,ε = 0. 01- 0. 1 s-1)with about 33% peak efficiency of power dissipation( η). Cracks was expected in two domains at either lower temperatures( < 1 000 ℃) or low strain rates( 0. 001 s-1) with different cracking mechanisms. Flow localization occurred when the strain rates exceeded 1 s-1 at all testing temperatures.
引用
收藏
页码:501 / 508
页数:8
相关论文
共 21 条
[11]  
Processing map and hot working mechanisms in a P/M TiAl alloy composite with in situ carbide and silicide dispersions[J] . K.P. Rao,Y.V.R.K. Prasad.Materials Science & Engineering A . 2010 (24)
[12]  
Influence of oxygen on the processing maps for hot working of electrolytic tough pitch copper[J] . Y.V.R.K. Prasad,K.P. Rao.Materials Letters . 2006 (21)
[13]  
Hot workability of spray-formed AISI M3:2 high-speed steel[J] . C. Rodenburg,M. Krzyzanowski,J.H. Beynon,W.M. Rainforth.Materials Science & Engineering A . 2004 (1)
[14]   Investigation on hot deformation behavior of AISI T1 high-speed steel [J].
Liu, JT ;
Chang, HB ;
Wu, RH ;
Hsu, TY ;
Ruan, XY .
MATERIALS CHARACTERIZATION, 2000, 45 (03) :175-186
[15]  
On the evolution of porosity in spray-deposited tool steels[J] . Haiming Hu,Enrique J. Lavernia,Zin H. Lee,Dawn R. White.Metallurgical and Materials Transactions A . 2000 (3)
[16]   Different carbide types and their effect on bend properties of a spray-formed high speed steel [J].
Lee, ES ;
Park, WJ ;
Baik, KH ;
Ahn, S .
SCRIPTA MATERIALIA, 1998, 39 (08) :1133-1138
[17]  
Fundamentals of creep and creep rupture in metals, Mac Millan, N. Garofalo F. Y . 1965
[18]  
Hot working characteristics of steels in austenitic state[J] . H.J. McQueen,S. Yue,N.D. Ryan,E. Fry.Journal of Materials Processing Tech. . 1995 (1)
[19]  
Microstructural changes in As— Cast M2[J] . M. R. Ghomashchi,CM. Sellars.Metallurgical Transactions A . 1993 (10)
[20]  
Hot workability of three grades of tool steel[J] . C. Imbert,N. D. Ryan,H. J. McQueen.Metallurgical Transactions A . 1984 (10)