Analysis of europium doped luminescent barium thioaluminate

被引：0

作者：

张东璞 ^{[1
]}

喻志农 ^{[1
]}

薛唯 ^{[1
]}

章婷 ^{[1
]}

丁瞾 ^{[1
]}

王武育 ^{[2
]}

机构：

[1] School of Optoelectronics,Beijing Institute of Technology

[2] Division of Mineral & Metallurgical Materials,Beijing General Research Institute for Non-Ferrous Metals

来源：

Journal of Rare Earths | 2010年 / 28卷 / 02期

关键词：

inorganic electroluminescence; Ba-Al-S:Eu; powder-sintering; RF-sputtering; photoluminescence; rare earths;

D O I：

暂无

中图分类号：

O614.33 [镧系元素（稀土元素）];

学科分类号：

070301 ; 081704 ;

摘要：

Europium-doped barium thioaluminate sputtering target was synthesized by powder sintering method and thin film was deposited by radio frequency(RF) sputtering.X-ray diffractometer(XRD) pattern indicated that the main compound of the target was BaAl4S7.Oxygen was the main impurity which led to the formation of BaAl2O4.It was shown that both BaAl4S7 and BaAl2S4 were contained in the as-grown thin films and a 471.7 nm emission peak in the PL spectra appeared due to a combination of BaAl4S7:Eu2+ and BaAl2S4:Eu2+.In addition,the product of oxidation in the film was BaSO4 instead of BaAl2O4 and led to an emission peak at 415.2 nm in the PL spectra assigned to the f→f transition of Eu2+ in the BaSO4 host.

引用

页码：185 / 188

页数：4

共 13 条

[11]

Synthesis and Photoluminescence of MIIM2III(S,Se)4. Donohue P C,,Hanlon J E. Journal of the Electrochemical Society . 1974

[12]

Atomic composition and structural properties of blue emitting BaAl2S4:Eu electroluminescent thin films. Inoue Y,Tanaka I,Tanaka K,Izumi Y,Okamoto S,Kawanishi M,Barada D,Miura N,Matsumoto H,Nakano R. Japanese Journal of Applied Physics Part1 . 2001

[13]

Crystallographic and luminescent properties of orthorhombic BaAl2S4:Eu powder and thin films. Smet P F,Van Haecke J E,Van Meirhaghe R L,Poelman D. Journal of Applied Physics . 2005

← 1 2 →