Corrosion and high-temperature oxidation of AM60 magnesium alloy

被引：2

作者：

芦笙 ^{[1
]}

周晓燕 ^{[1
]}

陈静 ^{[2
]}

侯志丹 ^{[1
]}

机构：

[1] Department of Materials Science and Engineering,Jiangsu University of Science and Technology

[2] Department of Mechanical Engineering, Jiangsu University of Science and Technology

来源：

Transactions of Nonferrous Metals Society of China | 2007年 / S1期

关键词：

AM60 magnesium alloy; corrosion; oxidation; microstructure; aging;

D O I：

暂无

中图分类号：

TG174.3 [腐蚀试验及设备];

学科分类号：

080503 ;

摘要：

The corrosion and high-temperature oxidation characteristics of AM60 Mg alloy in different environments were investigated by immersion test,electrochemical polarizing analysis and differential thermal analysis(DTA)/thermo gravimetric(TG) experiments. The influence of aging heat treatment on the corrosion resistance of AM60 Mg alloy was studied. AM60 Mg alloy shows better corrosion resistance in sea water than in 3.5%(mass fraction) NaCl solution. The corrosion resistance after aging for 24 h is better than that of both as-cast and aging for 48 h. Corrosion resistance of Mg alloy is controled by microstructure,composition of α-matrix. Precipitation of β phase along the grain boundaries acts as a barrier that decreases corrosion rate,whereas the decrease of aluminum content of α phase causes an increase in the corrosion rate. The DTA and TG curves of heating process in air are characterized with combustion after 590 ℃. When heated in helium,the curves show two endothermic peaks and a remarkable evaporation of magnesium. As for isothermal DTA and TG experiments,mass increment caused by oxidation does not happen till 520 ℃.

引用

页码：156 / 160

页数：5

共 3 条

[1] Mg合金的最新发展及应用前景 [J].

曾荣昌 ;

柯伟 ;

徐永波 ;

韩恩厚 ;

朱自勇 ;

不详 .

金属学报 , 2001, (07) :673-685

[2] Evaluation of microstructural effects on corrosion behaviour of AZ91D magnesium alloy [J].

Ambat, R ;

Aung, NN ;

Zhou, W .

CORROSION SCIENCE, 2000, 42 (08) :1433-1455

[3]

Influence of microstructure on the corrosion of die-cast AZ91D. Song G,Atrens A,Dargusch M. Corrosion Science . 1999

← 1 →