CA SELECTS——Carbon & Graphite Fibers

被引：0
作者：
张引枝
刘振宇
机构：
来源：
新型碳材料 | 1992年 / 03期
关键词：
碳纤维网; 机械性能; 炭纤维; 新型碳材料; 力学性质; 复合材料; Carbon; Graphite Fibers; CA SELECTS;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
<正> 具有良好挠曲性能的抗冲击复合材料由40—97份聚氧化甲烯和60—63份涂有0.1—10％的热固性聚胺酯的碳纤维组成。例如,80份Iupital F20—01（聚氧化甲烯）和20份用1.0聚胺酯悬液涂复的碳纤维混合体的悬臂梁式冲击强度为5.2kg/cm2,弯曲强度1500kg/cm2,弯曲模量54000kg/cm2,热变形温度为163℃,而碳纤维改用1.5％环氧树脂悬
引用
收藏
页码：58 / 68
页数：11
相关论文
共 50 条
[21]   Interaction of Cu Melt with Graphite Fibers [J].
Sytschev, A. E. ;
Vadchenko, S. G. ;
Shchukin, A. S. ;
Busurina, M. L. .
INTERNATIONAL JOURNAL OF SELF-PROPAGATING HIGH-TEMPERATURE SYNTHESIS, 2022, 31 (01) :51-53
[22]   Wearable Wire-Shaped Symmetric Supercapacitors Based on Activated Carbon-Coated Graphite Fibers [J].
Wang, Chan ;
Hu, Kuan ;
Li, Wenjian ;
Wang, Huaying ;
Li, Hu ;
Zou, Yang ;
Zhao, Chaochao ;
Li, Zhe ;
Yu, Min ;
Tan, Puchuan ;
Li, Zhou .
ACS APPLIED MATERIALS & INTERFACES, 2018, 10 (40) :34302-34310
[23]   Fracture of carbon fibers [J].
Lavin, JG .
FIBER FRACTURE, 2002, :157-179
[24]   High-performance wearable supercapacitors fabricated with surface activated continuous filament graphite fibers [J].
Jia, Dedong ;
Yu, Xin ;
Chen, Tinghan ;
Wang, Shu ;
Tan, Hua ;
Liu, Hong ;
Wang, Zhong Lin ;
Li, Linlin .
JOURNAL OF POWER SOURCES, 2017, 358 :13-21
[25]   Surface analysis of carbon and carbon fibers for composites [J].
Sherwood, PMA .
JOURNAL OF ELECTRON SPECTROSCOPY AND RELATED PHENOMENA, 1996, 81 (03) :319-342
[26]   Graphite melting and properties of liquid carbon [J].
Korobenko, VN ;
Savvatimski, AI ;
Cheret, R .
INTERNATIONAL JOURNAL OF THERMOPHYSICS, 1999, 20 (04) :1247-1256
[27]   Graphite Melting and Properties of Liquid Carbon [J].
V. N. Korobenko ;
A. I. Savvatimski ;
R. Cheret .
International Journal of Thermophysics, 1999, 20 :1247-1256
[28]   EFFECT OF CHEMISORBED OXYGEN ON THE ELECTROCHEMICAL-BEHAVIOR OF GRAPHITE FIBERS [J].
FRYSZ, CA ;
SHUI, XP ;
CHUNG, DDL .
CARBON, 1994, 32 (08) :1499-1505
[29]   Carbon fibers from kerosene [J].
Sharon, M ;
Kumar, M ;
Kichambare, PD ;
Ando, Y ;
Zhao, XL .
DIAMOND FILMS AND TECHNOLOGY, 1998, 8 (03) :143-152
[30]   Carbon nanotube nanocomposite fibers [J].
Moisan, Sandy ;
Poulin, Philippe ;
Derre, Alain .
ACTUALITE CHIMIQUE, 2009, (336) :31-35
12345