StructuresandPropertiesofLa0.8Sr0.2MnO3+σ-zSBA-15（z=0,1,2,4）PerovskiteCatalysts

Mesoporous La0.8Sr0.2MnO3+σ/z SBA-15（z = 1, 2, 4） perovskite oxides were synthesized via hard-templating with ordered mesoporous silica SBA-15 as the template. The as-prepared samples were characterized by XRD, SEM, AFM, BET, and XPS and the catalytic activity was tested for CO oxidation. The wide-angle XRD patterns showed that La0.8Sr0.2MnO3+σ perovskite was formed. The SEM and AFM analyses exhibited that La0.8Sr0.2MnO3+σ by hard-templating method had much smaller particle size（18 nm） than that（40 nm） by the sol-gel method. The perovskite-type oxides La0.8Sr0.2MnO3+σ/z SBA-15（z = 1, 2, 4） also displayed a higher BET surface area from 70 to 143.7 m2/g and a disordered mesostructure from nitrogen sorption analysis, as well as a small-angle XRD pattern. Moreover, the La0.8Sr0.2MnO3+σ/z SBA-15（z = 1, 2, 4） perovskite exhibited a much higher activity in CO oxidation than the conventional La0.8Sr0.2MnO3+σ perovskite. Further analysis by the means of XPS techniques indicated that the existence of high content of Oads/Olatt species contributed to the high activity.