Mechanical properties of underwater friction stir welded 2219 aluminum alloy

被引：0

作者：

刘会杰

张会杰

黄永宪

于雷

机构：

[1] StateKeyLaboratoryofAdvancedWeldingProductionTechnology,HarbinInstituteofTechnology

来源：

Transactions of Nonferrous Metals Society of China | 2010年 / 20卷 / 08期

关键词：

aluminum alloy; underwater friction stir welding; mechanical property;

D O I：

暂无

中图分类号：

TG457.1 [金属材料的焊接];

学科分类号：

080201 ; 080503 ;

摘要：

Underwater friction stir welding of 2219 aluminum alloy was carried out in order to further improve the joint performances by varying welding temperature history.The results indicated that the tensile strength of the joint can be improved from 324 MPa by external water cooling action in normal to 341 MPa.However,the plasticity of the joint is deteriorated.The underwater joint tends to fracture at the interface between the weld nugget zone and the thermal mechanically affected zone on the advancing side during tensile test,which is significantly different from the normal joint.

引用

页码：1387 / 1391

页数：5

共 6 条

[1]

Grain structure and dislocation density measurements in a friction-stir welded aluminum alloy using X-ray peak profile analysis.[J].Wanchuck Woo;Levente Balogh;Tamás Ungár;Hahn Choo;Zhili Feng.Materials Science & Engineering A.2008, 1

[2] Microstructure-microhardness relationships in friction stir welded AA5251 [J].

Attallah, Moataz M. ;

Davis, Claire L. ;

Strangwood, Martin .

JOURNAL OF MATERIALS SCIENCE, 2007, 42 (17) :7299-7306

[3] Microhardness prediction in friction stir welding of 2014 aluminium alloy [J].

Zhao, YH ;

Lin, SB ;

He, ZQ ;

Wu, L .

SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2006, 11 (02) :178-182

[4] Quantitative investigation of precipitation and mechanical behaviour for AA2024 friction stir welds [J].

Genevois, C ;

Deschamps, A ;

Denquin, A ;

Doisneau-cottignies, B .

ACTA MATERIALIA, 2005, 53 (08) :2447-2458

[5]

Friction stir welding and processing.[J].R.S. Mishra;Z.Y. Ma.Materials Science & Engineering R.2005, 1

[6] Microstructure and mechanical properties of friction stir welded aluminium alloys with special reference to AA 5083 and AA 6082 [J].

Svensson, LE ;

Karlsson, L ;

Larsson, H ;

Karlsson, B ;

Fazzini, M ;

Karlsson, J .

SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2000, 5 (05) :285-296

← 1 →