Anisotropic Creep Rupture Properties of a Nickel-base Single Crystal Superalloy at High Temperature

被引：0

作者：

Shaohua ZhangJian Zhang and Langhong Lou Superalloys DivisionInstitute of Metal ResearchChinese Academy of SciencesShenyang China Shenyang National Laboratory for Materials ScienceInstitute of Metal ResearchChinese Academy of SciencesShenyang China ^{[1
,1
,2
,1
,1
,110016
,2
,110016
]}

机构：

来源：

JournalofMaterialsScience&Technology | 2011年 / 27卷 / 02期

关键词：

Nickel-base single crystal superalloy; Stress rupture property; Orientation; Dislocation;

D O I：

暂无

中图分类号：

TG132.32 [];

学科分类号：

080502 ;

摘要：

The creep rupture properties of a single crystal superalloy were tested at 975℃/255 MPa as a function of the deviation degrees from [001].The misorientation of the specimens away from [001] distributed approximately along a line between [001]-[011] and [001]-[111] boundaries in the triangle of the stereographic projection.Creep rupture lifetimes of the specimens were not sensitive to the misorientation until the deviation degree exceeded ～30 deg.Two steps of lattice rotation were found in all specimens during creep,first towards the [001]-[111] boundary,and then to [001] or [111] along the boundary.Single slip and strong asymmetric deformation were observed during the first stage of lattice rotation in specimens with large misorientation.The rotation mechanism was associated with the activated slip systems according to the calculated Schmid factors.The impact of lattice rotation on the rupture properties was also discussed.

引用

页码：107 / 112

页数：6

共 8 条

[1] On the primary creep of CMSX-4 superalloy single crystals [J].

Rae, CMF ;

Matan, N ;

Cox, DC ;

Rist, MA ;

Reed, RC .

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2000, 31 (09) :2219-2228

[2] The breakdown of single-crystal solidification in high refractory nickel-base alloys [J].

Pollock, TM ;

Murphy, WH .

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1996, 27 (04) :1081-1094

[3] THE MECHANISMS OF FORMATION AND PREVENTION OF CHANNEL SEGREGATION DURING ALLOY SOLIDIFICATION [J].

SAMPLE, AK ;

HELLAWELL, A .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1984, 15 (12) :2163-2173

[4] THE INFLUENCE OF ORIENTATION ON THE STRESS RUPTURE PROPERTIES OF NICKEL-BASE SUPER-ALLOY SINGLE-CRYSTALS [J].

MACKAY, RA ;

MAIER, RD .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1982, 13 (10) :1747-1754

[5] CREEP OF PRECIPITATION-HARDENED NICKEL-BASE ALLOY SINGLE-CRYSTALS AT HIGH-TEMPERATURES [J].

LEVERANT, GR ;

KEAR, BH ;

OBLAK, JM .

METALLURGICAL TRANSACTIONS, 1973, 4 (01) :355-362

[6]

The origin of freckles in unidirectionally solidified castings[J] . S. M. Copley,A. F. Giamei,S. M. Johnson,M. F. Hornbecker.Metallurgical Transactions . 1970 (8)

[7]

On the nature of freckles in nickel base superalloys[J] . A. F. Giamei,B. H. Kear.Metallurgical Transactions . 1970 (8)

[8]

The mechanism of creep in gamma prime precipitation-hardened nickel-base alloys at intermediate temperatures[J] . Gerald R. Leverant,Bernard H. Kear.Metallurgical and Materials Transactions B . 1970 (2)

← 1 →