EffectofheattreatmentonelectroresistanceinNd0.67Sr0.33MnO3ceramics

被引:1
作者
陈顺生
王瑞龙
王浩
杨昌平
机构
[1] TheProvincialKeyLaboratoryofPiezoelectricCeramicsMaterialsandApparatus,FacultyofPhysicsandElectronicTechnology,HubeiUniversity
关键词
colossal electroresistance; perovskite; heat treatment; microstructure; rare earths;
D O I
暂无
中图分类号
TQ174.1 [基础理论];
学科分类号
0805 ; 080502 ;
摘要
A remarkable CER(colossal electroresistance) effect was observed in a series of polycrystalline Nd0.67Sr0.33MnO3 samples synthe-sized by high energy ball milling successive heat treatment.The CER ratio increased with increasing heating time and reached 3580% at a low temperature for the Nd0.67Sr0.33MnO3 ceramic annealed up to 13 h as measuring current was enhanced from 5 to 500 μA.The result showed that the CER effect was strongly dependent on the sample's microstructure,especially on the foreign phases which were gradually developed within grain boundaries when annealing time was more than 3 h.
引用
收藏
页码:251 / 254
页数:4
相关论文
共 2 条
[1]  
Boundary resistance anomalies in Nd 0.7 Sr 0.3 MnO 3- δ[J] . Physica B: Physics of Condensed Matter . 2003 (1)
[2]   Phase stabilities of LnMn(2)O(5) (Ln=rare earth) [J].
Satoh, H ;
Suzuki, S ;
Yamamoto, K ;
Kamegashira, N .
JOURNAL OF ALLOYS AND COMPOUNDS, 1996, 234 (01) :1-5