Reheating Austenitizing Temperature of Spring Steel 60Si2MnA for Railway

被引：0

作者：

CUI JuanLIU YazhengPAN HuiGAO LifengSchool of Materials Science and EngineeringUniversity of Science and Technology BeijingBeijingChinaTechnology CenterXingtai Iron and Steel Co LtdXingtai HebeiChinaQuality Control DepartmentXingtai Iron and Steel Co LtdXingtai HebeiChina ^{[1
,2
,1
,1
,3
,1
,100083
,2
,54027
,3
,54027
]}

机构：

来源：

Journal of Iron and Steel Research(International) | 2008年 / 06期

关键词：

austenitizing temperature; austenite grain; pearlite interlamellar spacing; hardness; toughness;

D O I：

10.13228/j.boyuan.issn1006-706x.2008.06.012

中图分类号：

TG142.15 [];

学科分类号：

080502 ;

摘要：

The microsturctural transformation of austenite grain,pearlite interlamellar spacing,and lamellar cementite thickness of spring steel 60Si2MnA for railway were studied in the hot-rolled and reheated states.Furthermore,the effect of microstructural characterization on its final mechanical properties was discussed.The results showed that as far as 60Si2MnA,the pearlite interlamellar spacing determined the hardness,whereas,the austenite grain determined the toughness.Compared with microstructure and mechanical properties in the hot-rolled state,after reheating treatment at 950 ℃,its average grain sizes are apparently fine and the pearlite interlamellar spacing and lamellar cementite thickness coarsen to some extent,but both hardness and impact toughness increase to HRC 48 and 8.5 J,respectively.In the course of making spring,the optimum reheating austenitizing temperature for the 60Si2MnA steel is 950 ℃.

引用

页码：62 / 67

页数：6

共 5 条

[1] 50CrVA钢奥氏体晶粒粗化行为的研究 [J].

王轶农 ;

贾怀远 ;

史英春 ;

于学东 .

佳木斯工学院学报, 1994, (03) :131-134

[2] Comment on "Effect of interlamellar spacing on cementite dissolution during wire drawing of pearlitic steel wires" [J].

Gavriljuk, VG .

SCRIPTA MATERIALIA, 2001, 45 (12) :1469-1472

[3]

Effect of interlamellar spacing on the mechanical properties of 0.65% C steel[J] . O.P Modi,N Deshmukh,D.P Mondal,A.K Jha,A.H Yegneswaran,H.K Khaira.Materials Characterization . 2001 (5)

[4]

Development of a new-type suspension spring for rally cars[J] . Kotaro Watanabe,Masashi Tamura,Ken Yamaya,Takahiko Kunoh.Journal of Materials Processing Tech. . 2001 (1)

[5]

Effects of alloy additions and tempering temperature on the sag resistance of Si–Cr spring steels[J] . Won Jong Nam,Chong Soo Lee,Deok Young Ban.Materials Science ＆ Engineering A . 2000 (1)

← 1 →